Torlon® AI-30 LM

Категория	PAI, Polyamide-imide
Производитель	Solvay Specialty Polymers
Торговая марка	Torlon®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	zytQ0c_Torlon-AI-30-LM.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

Torlon® AI-30 LM is a wet polymer granule developed for the performance coatings industry. This polyamide-imide precursor consists of roughly 35% polymer solids, 63% water and 2% NMP. The high acid number of the polymer backbone allows the formulation of aqueous solutions with the addition of an appropriate complexing amine. Aqueous-based solutions made with Torlon® AI-30 LM have inherently low VOCs, which helps end users meet stringent environmental regulations.

Coatings based on the Torlon® AI-30 LM polymer yield durable, abrasion-resistant, thermally-stable films. The cured resin has superior resistance to organic solvents and a wide array of other commercial and industrial chemicals. Outstanding tribological characteristics are afforded both by the resin as well as its unparalleled intra-coat adhesion to fluoropolymers.

Aqueous-based AI-30 LM polymer coatings offer a sustainable solution for electrical/electronic, high temperature decorative and corrosion preventative applications. In addition, magnet wire insulation and protective coatings for printed circuit boards may be converted from solvent-borne (NMP) polyamide-imide solutions. Industrial applications include primers and decorative topcoats for cookware, appliances and housewares. Aqueous AI-30 LM polymer solutions may be easily combined with aqueous fluoropolymer dispersions to produce sustainable, high-performance, low-friction, corrosion-resistant coatings that provide protection to industrial and automotive parts.

Главная Информация
Характеристики	Хорошая стойкость к истиранию Хорошая адгезия Хорошая химическая стойкость Теплостойкость, высокая Водорастворимый Огнестойкий
Используется	Нанесение покрытия Клей
Соответствие RoHS	Свяжитесь с производителем
Внешний вид	Желтый
Формы	Порошок
Метод обработки	Лечение раствора Покрытие

Физический	Номинальное значение	Единица измерения
Молекулярный вес
Mn	3500	g/mol
Mw	11000	g/mol
Содержание твердых веществ	35	%
Кислотная ценность	125.00	mg KOH/g

Дополнительная информация
Solution ProcessingWaterborne polyamide-imide solutions may be formulated using Torlon® AI-30 LM and an appropriate complexing amine. Please contact your Solvay representative for further details. Waterborne PAI solutions are patent protected (US 6,479,581).ApplicationThere are numerous methods by which waterborne Torlon® AI-30 LM resin-based coatings can be effectively applied. Depending on the aesthetic and performance characteristics required, uniform coatings can be applied by spray, roll, spin or curtain techniques. Usually, dry film thicknesses from 5-10 µm are readily achieved in a single coating pass, with multi-coat systems affording the opportunity for even further surface build. Regardless of the method employed, it is essential to assure appropriate preparation of the substrate prior to application of coating. Once complete, application equipment should be purged of the coating and cleaned with water.Drying/CuringCoatings based upon Torlon® AI-30 LM resin dry and initiate cure at temperatures as low as 150°C (300°F). However, optimal film properties result after heating for 5 to 20 minutes at 275°C (527°F), depending on the film thickness and the formulation. In the case of multi-coat systems, an intermediate temperature step at around 200°C (390°F) for 10 minutes may be advisable. For coating formulations employing low solids, a brief flash off period of about 3 to 10 minutes may be recommended prior to initiating cure.

Дополнительная информация

Solution ProcessingWaterborne polyamide-imide solutions may be formulated using Torlon® AI-30 LM and an appropriate complexing amine. Please contact your Solvay representative for further details. Waterborne PAI solutions are patent protected (US 6,479,581).ApplicationThere are numerous methods by which waterborne Torlon® AI-30 LM resin-based coatings can be effectively applied. Depending on the aesthetic and performance characteristics required, uniform coatings can be applied by spray, roll, spin or curtain techniques. Usually, dry film thicknesses from 5-10 µm are readily achieved in a single coating pass, with multi-coat systems affording the opportunity for even further surface build. Regardless of the method employed, it is essential to assure appropriate preparation of the substrate prior to application of coating. Once complete, application equipment should be purged of the coating and cleaned with water.Drying/CuringCoatings based upon Torlon® AI-30 LM resin dry and initiate cure at temperatures as low as 150°C (300°F). However, optimal film properties result after heating for 5 to 20 minutes at 275°C (527°F), depending on the film thickness and the formulation. In the case of multi-coat systems, an intermediate temperature step at around 200°C (390°F) for 10 minutes may be advisable. For coating formulations employing low solids, a brief flash off period of about 3 to 10 minutes may be recommended prior to initiating cure.

Тип материала	Категория	Производитель
TECATOR™ GF30	PAI	Ensinger Inc.
Duratron® T4501	PAI	Quadrant Engineering Plastic Products
Duratron® T7130	PAI	Quadrant Engineering Plastic Products
Duratron® T4503	PAI	Quadrant Engineering Plastic Products
Torlon® 4203L	PAI	Solvay Specialty Polymers
Torlon® 4435	PAI	Solvay Specialty Polymers