Описание материалов:
In recent years, industry has demanded a range of materials that not only possess strength, wear properties, heat and chemical resistance but materials that are less resistive to the build-up of a static charge. Ensinger has a family of such materials; their properties are listed on the reverse side of this sheet and described below.
TECASINT™ 5201 has the highest compressive strength and use temperature of the group. It is based on an Ensinger manufactured polyamide imide resin with a low sloughing, additive package.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Хорошая прочность
- Хорошая химическая стойкость
- Хорошая стойкость к истиранию
|
| Формы | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.54 | g/cm³ | ASTM D792 |
| Поглощение воды (Equilibrium) | 0.47 | % | ASTM D570 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра | 93 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 4000 | MPa | ASTM D638 |
| Прочность на растяжение (Break) | 84.8 | MPa | ASTM D638 |
| Удлинение при растяжении (Break) | 4.0 | % | ASTM D638 |
| Flexural Strength | 134 | MPa | ASTM D790 |
| Прочность на сжатие | 240 | MPa | ASTM D695 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура непрерывного использования | 313 | °C | |
| CLTE-
Поток | 4.1E-5 | cm/cm/°C | ASTM D696 |
| Heat Deflection Temperature | 316 | °C | ASTM D648 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельное сопротивление поверхности | 1.0E+9 - 1.0E+12 | ohms | ASTM D257 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость | V-0 | | UL 94 |
| Дополнительная информация |
|---|
| Data obtained from extruded shapes material. |