Описание материалов:
Duratron® T5530 is 30% glass reinforced, compression molded PAI. It is ideal for higher load structural or electronic applications. This grade is similar in composition to Duratron® T5030 PAI. It is selected for larger shapes or when the greatest degree of dimensional control is required.
Duratron® PLA is the highest performing melt processable plastic. It has superior resistance to elevated temperatures. It is capable of performing under severe stress conditions at continuous temperatures to 500°F (260°C). Parts machined from Duratron® PLA stock shapes provide greater compressive strength and higher impact resistance than most advanced engineering plastics. Its extremely low coefficient of linear thermal expansion and high creep resistance deliver excellent dimensional stability over its entire use range. Duratron® PLA is an amorphous material with a Tg (glass transition temperature) of 537°F (280°C).
Data provided by Quadrant Engineering Plastic Products from tests on stock shapes and parts produced by Quadrant EPP.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Стекловолокно, 30% наполнитель по весу
|
| Характеристики | - Кислотоупорный
- Устойчивость к воздействию алкоголя
- Аморфный
- Хорошая химическая стойкость
- Хорошая прочность на сжатие
- Хорошее сопротивление ползучести
- Хорошая стабильность размеров
- Хорошая жесткость
- Хорошая термическая стабильность
- Хорошая износостойкость
- Высокая ударопрочность
- Высокая прочность
- Устойчивость к углеводородам
- Устойчивость к растворителям
|
| Используется | - Электрическое/электронное применение
- Детали конструкции
|
| Формы | - Настраиваемые Формы
- Диск
- Предварительно сформированные детали
- Стержень
- Лист
- Трубка
|
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.61 | g/cm³ | ASTM D792 |
| Поглощение воды | | | ASTM D570 |
| 24 hr | 0.30 | % | |
| Saturation | 1.5 | % | |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла | | | ASTM D785 |
| E-Scale | 85 | | |
| M-Scale | 125 | | |
| Твердость дюрометра (Shore D) | 90 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 6210 | MPa | ASTM D638 |
| Прочность на растяжение (Ultimate) | 103 | MPa | ASTM D638 |
| Удлинение при растяжении (Break) | 3.0 | % | ASTM D638 |
| Флекторный модуль | 6210 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 138 | MPa | ASTM D790 |
| Компрессионный модуль | 4140 | MPa | ASTM D695 |
| Прочность на сжатие (10% Strain) | 186 | MPa | ASTM D695 |
| Коэффициент трения (vs. Steel - Static) | 0.20 | | Internal Method |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | 37 | J/m | ASTM D256A |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке (1.8 MPa, Unannealed) | 271 | °C | ASTM D648 |
| Максимальная температура использования-
Долгосрочный, воздушный | 260 | °C | |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Limiting Pressure Velocity 1 | 0.701 | MPa·m/s | Internal Method |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура перехода стекла | 275 | °C | ASTM D3418 |
| CLTE-
Поток 2(-40 to 149°C) | 4.7E-5 | cm/cm/°C | ASTM E831 |
| Теплопроводность | 0.36 | W/m/K | ASTM F433 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельное сопротивление поверхности 3 | > 1.0E+13 | ohms | Internal Method |
| Диэлектрическая прочность 4 | 28 | kV/mm | ASTM D149 |
| Диэлектрическая постоянная (1 MHz) | 6.30 | | ASTM D150 |
| Коэффициент рассеивания (1 MHz) | 0.050 | | ASTM D150 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость (3.18 mm, Estimated Rating) | V-0 | | UL 94 |
| Примечание |
|---|
| 1 . | 4:1 safety factor |
| 2 . | 68°F |
| 3 . | EOS/ESD S11.11 |
| 4 . | Method A (Short-Time) |