Описание материалов:
Duratron® T4540 compression molded PAI is a seal and bearing grade offers a very low coefficient of friction and good wear properties. It was developed specifically for use in rotating equipment. Its composition is the same as the former Duratron® T4340 polyamide-imide and used when larger (especially tubular) shapes are required. Typical applications for Duratron® T4540 PAI include labyrinth seals, wear rings, bushings, and bearings of all types.
Duratron® PLA is the highest performing melt processable plastic. It has superior resistance to elevated temperatures. It is capable of performing under severe stress conditions at continuous temperatures to 500°F (260°C). Parts machined from Duratron® PLA stock shapes provide greater compressive strength and higher impact resistance than most advanced engineering plastics. Its extremely low coefficient of linear thermal expansion and high creep resistance deliver excellent dimensional stability over its entire use range. Duratron® PLA is an amorphous material with a Tg (glass transition temperature) of 537°F (280°C).
Data provided by Quadrant Engineering Plastic Products from tests on stock shapes and parts produced by Quadrant EPP.
| Главная Информация | |
|---|
| Характеристики | - Кислотоупорный
- Устойчивость к воздействию алкоголя
- Аморфный
- Хорошая химическая стойкость
- Хорошая прочность на сжатие
- Хорошее сопротивление ползучести
- Хорошая стабильность размеров
- Хорошая жесткость
- Хорошая термическая стабильность
- Хорошая износостойкость
- Высокая ударопрочность
- Высокая прочность
- Устойчивость к углеводородам
- Устойчивость к растворителям
|
| Используется | - Подшипники
- Втулки
- Вращающееся оборудование
- Уплотнительные устройства
- Уплотнения
|
| Формы | - Настраиваемые Формы
- Диск
- Предварительно сформированные детали
- Лист
- Трубка
|
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.46 | g/cm³ | ASTM D792 |
| Поглощение воды | | | ASTM D570 |
| 24 hr | 0.30 | % | |
| Saturation | 1.5 | % | |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла | | | ASTM D785 |
| E-Scale | 66 | | |
| M-Scale | 107 | | |
| Твердость дюрометра (Shore D) | 90 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 3960 | MPa | ASTM D638 |
| Прочность на растяжение (Ultimate) | 89.6 | MPa | ASTM D638 |
| Удлинение при растяжении (Break) | 5.0 | % | ASTM D638 |
| Флекторный модуль | 4690 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 165 | MPa | ASTM D790 |
| Компрессионный модуль | 2410 | MPa | ASTM D695 |
| Прочность на сжатие (10% Strain) | 117 | MPa | ASTM D695 |
| Коэффициент трения (vs. Steel - Static) | 0.20 | | Internal Method |
| Коэффициент износа | 640 | 10^-8 mm³/N·m | ASTM D3702 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | 59 | J/m | ASTM D256A |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке (1.8 MPa, Unannealed) | 279 | °C | ASTM D648 |
| Максимальная температура использования-
Долгосрочный, воздушный | 260 | °C | |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Limiting Pressure Velocity 1 | 0.263 | MPa·m/s | Internal Method |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура перехода стекла | 275 | °C | ASTM E1356 |
| CLTE-
Поток 2(-40 to 149°C) | 3.6E-5 | cm/cm/°C | ASTM E831 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельное сопротивление поверхности 3 | 1.0E+13 | ohms | Internal Method |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость (3.18 mm, Estimated Rating) | V-0 | | UL 94 |
| Примечание |
|---|
| 1 . | 4:1 safety factor |
| 2 . | 68°F |
| 3 . | EOS/ESD S11.11 |