Описание материалов:
Halar558 fluoropolymer resin grades are used for foam extrusion products, including main insulating materials, coaxial cable cores, cross-laying nets, fire alarm cables, sheaths and foam pipes. Like other Halar resin grades, this grade resin can adapt to a wide range of use temperatures from low temperature to 150 ℃, and has excellent chemical resistance to various acids, alkalis, organic solvents, etc. Cables containing Halar 558 materials meet the fire performance requirements of NFPA 90A (Air Conditioning and Ventilation System Standard). In order to meet these requirements, materials must pass NFPA 262 flame propagation and wire and cable smoke standard test methods. In addition, even Halar 558 resin thin-walled parts have excellent mechanical properties. The resin melts at 242 ℃, and its polymer chain is mainly composed of ethylene and chlorotrifluoroethylene alternately arranged in 1:1 units. Halar ECTFE can be machined with most standard metalworking machine tools. Due to the low thermal conductivity of the material, it may cause heat accumulation. It is recommended to use a coolant to prevent the parts from softening during processing.
| Главная Информация | |
|---|
| Добавка | - Нуклеативный агент
- Пенообразователь
- Вспомогательные средства для обработки
|
| Характеристики | - Ядро
- Основа для защиты от растворителей
- Хорошая химическая стойкость
- Сопротивление щелочи
- Стойкость к кислоте
|
| Используется | - Кабельная оболочка
- Электронная изоляция
- Фитинги для труб
- Пена
|
| Рейтинг агентства | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.68 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) | 15 - 20 | g/10 min | ASTM D3275 |
| Поглощение воды (Equilibrium) | < 0.10 | % | ASTM D570 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура плавления | 242 | °C | DSC |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость | V-0 | | UL 94 |
| Индекс кислорода (1.60 mm) | 52 | % | ASTM D2863 |
| Дополнительная информация |
|---|
| 色母粒 - 与Halar树脂所有其它牌号一样，Halar 558可以很容易地用市售色母粒着色。当进行内层绝缘着色时，强烈建议用量不要超过重量的1%，因为色母粒会影响内层绝缘的电性能。 安全操作和使用
不建议在高于572°F (300°C)的温度下加工Halar 558含氟聚合物，会发生迅速热降解。当发生降解时， Halar 558会释放盐酸（HCL）和氢氟酸（HF ）这些即使在较低浓度下也会具有刺激性、腐蚀性和毒性的气体。请参阅塑料工业学会出版的塑料行业氟聚合树脂安全操作指南。。
为避免吸入分解后产品，建议正确利用局部排风罩或柔性管道，排出挤塑烟雾。如果处置不当，Halar 558可能会释放有毒有害化学物质。 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Зона цилиндра 1 темп. | 243 | °C | |
| Зона цилиндра 2 температура. | 249 | °C | |
| Зона цилиндра 3 темп. | 263 | °C | |
| Зона цилиндра 4 темп. | 280 | °C | |
| Температура фланца | | | |
| Falan 2 | 252 | °C | |
| Flange 1 | 252 | °C | |
| Максимальная температура | 243 | °C | |
| Температура поперечного носа | 254 | °C | |
| Температура фиксирующей пластины | 246 | °C | |
| Температура матрицы | 274 | °C | |
| Инструкции по экструзии |
|---|
| Halar558树脂是完全预混的含氟聚合物，含成核剂、在挤塑过程中分解的化学发泡剂以及加工助剂。有没有无需向系统注入氮气。可以通过调整熔融温度、头部压力和急冷速度等工艺条件，将部件内部的密闭气泡空隙按照0-70 ％的范围进行调节 。如果需要降至低发泡剂来减少气泡数量，可以在Halar558中混合Halar 500。 Halar 558已经通过各种不同的标准螺杆挤塑设备进行了加工，包括标准氟聚物的加工。可带或不带菠萝混合头；压缩比：3:1； 喂料/传送/压缩段螺杆深度分别为 12/5/9。具体应避免使用快速传输螺杆（ 1-2个螺槽深度）和的Maddox 混合机头。 设备/机械建议： -挤出头尺寸: 1~2.5英寸 -挤出机L/D：24：1 -筛网：40/60 -直角挤塑机头类型：固定或可调 -锥长：0.25英寸～0.75英寸 -线速度：最高1700fpm -模具：加压 -吹胀比：1.75～2.75 |