Описание материалов:
Jamplast ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. Jamplast ABS resins are available in a wide range of melt flow rates, impact strength and heat resistance for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion and thermoforming processes.
Automotive Jamplast ABS resins offer a wide range of gloss, viscosity, impact strength and heat properties for use in numerous automotive applications. Melt flow rates from 1 to 12 g/10 min, impact strengths from 2.5 to 12 ft-lb/in and heat distortion temperatures from 165°F to 190°F are available. Available primarily as natural plus concentrates, Jamplast ABS resins are used in a wide variety of automotive applications including structural instrument panels, consoles, pillars, and exterior trim parts requiring painting and plating.
Jamplast JPLGABSI ABS resin is a high flow, low gloss ABS resin often used in door panels, consoles, and various interior trim.
| Главная Информация | |
|---|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.04 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (230°C/3.8 kg) | 6.0 | g/10 min | ASTM D1238 |
| Формовочная усадка-
Поток | 0.40 to 0.70 | % | ASTM D955 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения 1 | 1790 | MPa | ASTM D638 |
| Прочность на растяжение 2(Yield) | 41.4 | MPa | ASTM D638 |
| Удлинение при растяжении 3(Yield) | 3.0 | % | ASTM D638 |
| Флекторный модуль 4 | 2070 | MPa | ASTM D790 |
| Flexural Strength 5 | 58.6 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact 6 | | | ASTM D256 |
| -18°C, 3.18 mm | 80 | J/m | |
| 23°C, 3.18 mm | 160 | J/m | |
| Ударное устройство для дротиков 7 | | | ASTM D3763 |
| 23°C, 3.18 mm, Peak Energy | 32.8 | J | |
| 23°C, 3.18 mm, Total Energy | 42.9 | J | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | ASTM D648 |
| 0.45 MPa, Unannealed, 3.18 mm | 90.6 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 76.7 | °C | |
| Викат Температура размягчения | 104 | °C | ASTM D1525 |
| CLTE-
Поток | 7.4E-5 | cm/cm/°C | ASTM D696 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 82.2 to 85.0 | °C | |
| Время сушки | 2.0 to 4.0 | hr | |
| Рекомендуемая максимальная влажность | 0.10 | % | |
| Температура обработки (расплава) | 232 to 246 | °C | |
| Температура формы | 26.7 to 48.9 | °C | |
| Back Pressure | 0.345 to 3.45 | MPa | |
| Тонаж зажима | 2.8 to 4.1 | kN/cm² | |
| Отношение винта L/D | 20.0:1.0 | | |
| Коэффициент сжатия винта | 1.5:1.0 to 3.5:1.0 | | |
| Примечание |
|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | Type I, 1.3 mm/min |
| 5 . | Type I, 1.3 mm/min |
| 6 . | 0.25 mm Notch Depth |
| 7 . | 3.39 m/sec |