Описание материалов:
Lustran ABS LK197 resin is a high-gloss, medium-impact extrusion grade of ABS (Acrylonitrile Butadiene Styrene). It provides a superior balance between rigidity and impact strength, as well as excellent melt strength for good thermoformability. It is easy to color with ABS color concentrates.
Lustran ABS LK197 resin is used for applications that require high gloss and higher rigidity, such as bathtubs, sinks, and shower surrounds for recreational vehicles, and interior liners for ice chests and picnic coolers. As with any product, use of Lustran ABS LK197 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Характеристики | - Жесткий, высокий
- Подсветка
- Хорошая прочность расплава
- Хорошая окраска
- Средняя ударопрочность
|
| Используется | - Подкладка
- Область архитектурного применения
- Спортивные товары
- Аксессуары для ванной комнаты
|
| Рейтинг агентства | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.06 | g/cm³ | ASTM D792 |
| Удельный объем | 0.940 | cm³/g | ASTM D792 |
| Массовый расход расплава (MFR) (230°C/10.0 kg) | 9.2 | g/10 min | ASTM D1238 |
| Поглощение воды 1(23°C, 24 hr) | 0.40 | % | ASTM D570 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale) | 113 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | | | ASTM D638 |
| -18°C | 2550 | MPa | ASTM D638 |
| 23°C | 2280 | MPa | ASTM D638 |
| 71°C | 1520 | MPa | ASTM D638 |
| Прочность на растяжение | | | ASTM D638 |
| Yield, -18°C | 59.3 | MPa | ASTM D638 |
| Yield, 23°C | 40.0 | MPa | ASTM D638 |
| Yield, 71°C | 22.1 | MPa | ASTM D638 |
| Флекторный модуль | | | ASTM D790 |
| -40°C | 2760 | MPa | ASTM D790 |
| 23°C | 2480 | MPa | ASTM D790 |
| 71°C | 1930 | MPa | ASTM D790 |
| Flexural Strength | | | ASTM D790 |
| Yield, -40°C | 114 | MPa | ASTM D790 |
| Yield, 23°C | 63.4 | MPa | ASTM D790 |
| Yield, 71°C | 49.6 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | | | ASTM D256 |
| -40°C, 3.18 mm | 91 | J/m | ASTM D256 |
| -18°C, 3.18 mm | 130 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 240 | J/m | ASTM D256 |
| Ударное устройство для дротиков | | | ASTM D3763 |
| -40°C, Peak Energy | 10.8 | J | ASTM D3763 |
| -40°C, Total Energy | 13.6 | J | ASTM D3763 |
| -18°C, Peak Energy | 19.0 | J | ASTM D3763 |
| -18°C, Total Energy | 24.4 | J | ASTM D3763 |
| 23°C, Peak Energy | 21.7 | J | ASTM D3763 |
| 23°C, Total Energy | 29.8 | J | ASTM D3763 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | ASTM D648 |
| 0.45 MPa, not annealed | 92.8 | °C | ASTM D648 |
| 0.45 MPa, annealed | 101 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 85.0 | °C | ASTM D648 |
| 1.8 MPa, annealed | 93.9 | °C | ASTM D648 |
| CLTE-
Поток | 9.0E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (1.47 mm) | 60.0 | °C | UL 746 |
| RTI Imp (1.47 mm) | 60.0 | °C | UL 746 |
| RTI Str (1.47 mm) | 60.0 | °C | UL 746 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Скорость горения 2(3.18 mm) | 36 | mm/min | SAE J1685 |
| Огнестойкость (1.47 mm) | HB | | UL 94 |
| Оптический | Номинальное значение | | Метод испытания |
|---|
| Блестящий Гарднер (60 °, extruded sheet) | 90 | | ASTM D523 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 82.2 - 93.3 | °C | |
| Время сушки | 3.0 - 4.0 | hr | |
| Рекомендуемая максимальная влажность | < 0.030 | % | |
| Зона цилиндра 1 темп. | 216 - 241 | °C | |
| Зона цилиндра 2 температура. | 216 - 241 | °C | |
| Зона цилиндра 3 темп. | 216 - 241 | °C | |
| Зона цилиндра 4 темп. | 216 - 241 | °C | |
| Зона цилиндра 5 темп. | 216 - 241 | °C | |
| Температура расплава | 216 - 249 | °C | |
| Температура матрицы | 210 - 241 | °C | |
| Рулон для снятия | 62.8 - 104 | °C | |
| Инструкции по экструзии |
|---|
| Compression Ratio: 2.5: to 2.7:1Pump Ratio: 1.5 to 2.0Max Regrind Allowed: 40% |
| Примечание |
|---|
| 1 . | Injection Molded specimen |
| 2 . | Injection Molded specimen |