Описание материалов:
Triax 1185 resin is an ABS (Acrylonitrile Butadiene Styrene)/Nylon 6 alloy for injection molding. It is a semicrystalline thermoplastic with excellent processibility, good chemical resistance, good fatigue performance, and excellent abrasion characteristics. Triax 1185 resin has excellent impact resistance across a broad temperature range and excellent surface appearance.
Triax 1185 resin is designed for use in large parts requiring a smooth finish and consistent appearance. Typical applications include components for recreational vehicles, snowmobiles, sporting goods, and a variety of parts for industrial and consumer applications. As with any product, use of Triax 1185 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Характеристики | - Полу-кристаллический
- Хорошая ударопрочность
- Обрабатываемость, хорошая
- Хорошая стойкость к истиранию
- Хорошая химическая стойкость
- Сопротивление усталости
- Отличный внешний вид
|
| Используется | - Промышленное применение
- Спортивные товары
- Применение потребительских товаров
|
| Рейтинг агентства | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.07 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (230°C/10.0 kg) | 20 | g/10 min | ASTM D1238 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 1400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 32.0 | MPa | ISO 527-2/50 |
| Флекторный модуль 1 | 1150 | MPa | ISO 178 |
| Флекторный стресс 2 | 45.0 | MPa | ISO 178 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | | | ISO 180 |
| -40°C | 28 | kJ/m² | ISO 180 |
| -30°C | 57 | kJ/m² | ISO 180 |
| 23°C | 81 | kJ/m² | ISO 180 |
| Многоосная инструментальная Энергия удара | | | ISO 6603-2 |
| -30°C, 2.54mm, energy to peak strength | 24.0 | J | ISO 6603-2 |
| -30°C, 2.54mm, total impact penetration energy | 44.0 | J | ISO 6603-2 |
| 23°C, 2.54mm, energy to peak strength | 20.0 | J | ISO 6603-2 |
| 23°C, 2.54mm, total impact penetration energy | 40.0 | J | ISO 6603-2 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature | | | |
| 0.45 MPa, not annealed | 80.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 52.0 | °C | ISO 75-2/A |
| Викат Температура размягчения | 190 | °C | ISO 306/A120 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 87.8 | °C | |
| Время сушки | 2.0 - 4.0 | hr | |
| Рекомендуемый размер снимка | 50 - 70 | % | |
| Рекомендуемый Макс измельчения | 20 | % | |
| Задняя температура | 232 - 266 | °C | |
| Средняя температура | 232 - 266 | °C | |
| Передняя температура | 232 - 266 | °C | |
| Температура сопла | 249 - 260 | °C | |
| Температура обработки (расплава) | 238 - 271 | °C | |
| Температура формы | 37.8 - 93.3 | °C | |
| Давление впрыска | 41.4 - 82.7 | MPa | |
| Скорость впрыска | Fast | | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Тонаж зажима | 4.1 - 6.9 | kN/cm² | |
| Подушка | < 3.18 | mm | |
| Отношение винта L/D | 20.0:1.0 | | |
| Коэффициент сжатия винта | 2.5:1.0 | | |
| Инструкции по впрыску |
|---|
| Hold Pressure: 30 to 50% of Injection PressureScrew Speed: Moderate |
| Примечание |
|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |