Описание материалов:
Triax 1315 resin is a 15% glass-reinforced ABS (Acrylonitrile Butadiene Styrene)/Nylon alloy for injection molding. It is a semicrystalline thermoplastic with excellent processibility, good chemical resistance, good fatigue performance, and excellent abrasion characteristics. Triax 1315 resin offers added strength, rigidity, and heat resistance.
Triax 1315 resin is used for parts requiring good rigidity and warpage control. Typical applications include housings, shrouds handles for components of lawn and garden equipment, power tools, appliances, and sporting goods. Automotive applications include fasteners and interior functional components, housings, and shrouds. As with any product, use of Triax 1315 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Армированный стекловолокном материал, 15% наполнитель по весу
|
| Характеристики | - Полу-кристаллический
- Низкий уровень защиты
- Жесткий, высокий
- Высокая прочность
- Обрабатываемость, хорошая
- Хорошая стойкость к истиранию
- Сопротивление усталости
- Теплостойкость, высокая
|
| Используется | - Ручка
- Оборудование для газонов и сада
- Электроприборы
- Электропитание/другие инструменты
- Крепежные детали
- Применение в автомобильной области
- Автомобильные внутренние детали
- Спортивные товары
- Чехол
|
| Рейтинг агентства | |
| Формы | |
| Метод обработки | |
| Многоточечные данные | - Изохронный стресс против деформации (ISO 11403-1)
- Изоляционный стресс против деформации (ISO 11403-1)
- Сектантный модуль против деформации (ISO 11403-1)
|
| Физический | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.17 | 1.17 | g/cm³ | ASTM D792 |
| Удельный объем | 0.850 | 0.850 | cm³/g | ASTM D792 |
| Формовочная усадка-
Поток | 0.45 | 0.45 | % | ASTM D955 |
| Твердость | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale) | 107 | 101 | | ASTM D785 |
| Механические | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 5170 | 4620 | MPa | ASTM D638 |
| Прочность на растяжение (Yield) | 82.7 | 75.2 | MPa | ASTM D638 |
| Удлинение при растяжении (Break) | 3.5 | 4.1 | % | ASTM D638 |
| Флекторный модуль | 4340 | 3760 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 130 | 112 | MPa | ASTM D790 |
| Воздействие | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | | | | ASTM D256 |
| -40°C, 3.18 mm | 69 | 69 | J/m | ASTM D256 |
| -40°C, 6.35 mm | 59 | 64 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 110 | 110 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 140 | 140 | J/m | ASTM D256 |
| Тепловой | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | | ASTM D648 |
| 0.45 MPa, unannealed, 3.18mm | 169 | 168 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 6.35mm | 190 | 180 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 98.9 | 97.2 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.35mm | 102 | 100 | °C | ASTM D648 |
| Викат Температура размягчения | 201 | 199 | °C | ASTM D1525 1 |
| CLTE-
Поток | | | | ASTM D696 |
| -40 to 22°C | 4.7E-5 | 4.5E-5 | cm/cm/°C | ASTM D696 |
| 22 to 83°C | 4.1E-5 | 4.0E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (1.50 mm) | 60.0 | 60.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 60.0 | 60.0 | °C | UL 746 |
| RTI Str (1.50 mm) | 60.0 | 60.0 | °C | UL 746 |
| Воспламеняемость | Сухой | Состояние | | Метод испытания |
|---|
| Огнестойкость | | | | UL 94 |
| 1.50 mm, Natural & Black | HB | HB | | UL 94 |
| 3.00 mm, Gray | HB | HB | | UL 94 |
| Оптический | Сухой | Состояние | | Метод испытания |
|---|
| Блестящий Гарднер | | | | ASTM D523 |
| 20° | 7 | 7 | | ASTM D523 |
| 60° | 26 | 26 | | ASTM D523 |
| Инъекция | Сухой | Единица измерения | |
|---|
| Температура сушки | 87.8 | °C | |
| Время сушки | 2.0 - 4.0 | hr | |
| Рекомендуемая максимальная влажность | 0.15 - 0.35 | % | |
| Рекомендуемый размер снимка | 50 - 70 | % | |
| Рекомендуемый Макс измельчения | 20 | % | |
| Задняя температура | 232 - 266 | °C | |
| Средняя температура | 232 - 266 | °C | |
| Передняя температура | 232 - 266 | °C | |
| Температура сопла | 249 - 260 | °C | |
| Температура обработки (расплава) | 238 - 271 | °C | |
| Температура формы | 37.8 - 65.6 | °C | |
| Давление впрыска | 41.4 - 82.7 | MPa | |
| Скорость впрыска | Fast | | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Тонаж зажима | 4.1 - 6.9 | kN/cm² | |
| Подушка | < 3.18 | mm | |
| Отношение винта L/D | 20.0:1.0 | | |
| Коэффициент сжатия винта | 2.5:1.0 | | |
| Инструкции по впрыску |
|---|
| Hold Pressure: 30 to 50% of Injection PressureScrew Speed: Moderate |
| Примечание |
|---|
| 1 . | 标准 B (120°C/h), 压 力1 (10N) |