Описание материалов:
Product Description
TOPAS 5013F-04 is a high temperature film extrusion grade for blends. It is a high clarity amorphous resin with high flow, high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and healthcare applications. It is used in monolayer cast blends, and in coextruded blends in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as heat resistant blister, hot fill, and easy tear packaging. If performance at elevated temperatures is not required, we also offer lower glass transition temperature (Tg) grades of TOPAS.
Selected Applications
Leading Attributes
Related Grades for Packaging and Film Extrusion
TOPAS 5013F-04 is a high temperature film extrusion grade for blends. It is a high clarity amorphous resin with high flow, high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and healthcare applications. It is used in monolayer cast blends, and in coextruded blends in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as heat resistant blister, hot fill, and easy tear packaging. If performance at elevated temperatures is not required, we also offer lower glass transition temperature (Tg) grades of TOPAS.
Selected Applications
- Decorative film and sheet
- General packaging
- Food packaging
- Blown film
- Healthcare and food contact
Leading Attributes
- Gloss, hardness, chemical resistance, forming
- Easy or linear tear, heat resistance, hot fill, gloss
- Not manufactured with BPA, phthalates, or halogens
- High strength and high productivity
- Broad regulatory compliance
Related Grades for Packaging and Film Extrusion
- TOPAS 6013F-04 - high temperature grade with standard flow
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 1.02 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | < 0.10 | g/10 min | ISO 1133 |
| 230°C/2.16 kg | 8.0 | g/10 min | ISO 1133 |
| Плавкий объем-расход (MVR) | ISO 1133 | ||
| 190°C/2.16 kg | < 0.100 | cm³/10min | ISO 1133 |
| 230°C/2.16 kg | 9.00 | cm³/10min | ISO 1133 |
| Поглощение воды (Saturation, 23°C) | 0.010 | % | ISO 62 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 70 | µm | |
| Модуль растяжения | ISO 527-3/1 | ||
| MD : 70 µm, cast film | 2600 | MPa | ISO 527-3/1 |
| TD : 70 µm, cast film | 2500 | MPa | ISO 527-3/1 |
| Tensile Stress | ISO 527-3/50 | ||
| MD : Fracture, 70 µm, cast film | 35.0 | MPa | ISO 527-3/50 |
| TD : Fracture, 70 µm, cast film | 25.0 | MPa | ISO 527-3/50 |
| Удлинение при растяжении | ISO 527-3/50 | ||
| MD : Fracture, 70 µm, cast film | 1.4 | % | ISO 527-3/50 |
| TD : Fracture, 70 µm, cast film | 1.1 | % | ISO 527-3/50 |
| Ударное падение Dart (70 µm, cast film) | < 36 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 70 µm, cast film | 0.11 | N | ISO 6383-2 |
| TD : 70 µm, cast film | 0.11 | N | ISO 6383-2 |
| Проницаемость кислорода (23°C, 70 µm, extruded film, 50% RH) | 26 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Скорость передачи водяного пара (70 µm, 38°C, Cast Film, 90% RH) | 0.14 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Температура перехода стекла | 134 | °C | ISO 11357-2 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (60, 70.0 µm, cast film) | > 100 | ISO 2813 | |
| Haze (70.0 µm, cast film) | < 1.0 | % | ISO 14782 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Кормовая часть экструдера | 20 - 70 | °C | |
| Экструдер винт L/D Соотношение | > 28:1 | ||
| Зона цилиндра 1 темп. | 220 - 240 | °C | |
| Зона цилиндра 2 температура. | 220 - 240 | °C | |
| Зона цилиндра 3 темп. | 220 - 240 | °C | |
| Зона цилиндра 4 темп. | 220 - 240 | °C | |
| Температура матрицы | 220 - 240 | °C |
| Инструкции по экструзии |
|---|
| Head pressure: P > 140 bar / 2000 psi; Fine screen packs as neededScrew Speed: RPM > 50% nominalScrew design: Multi-purpose or barrier screw with mixing section Screw diameter > 60 mm / 2.5 in Grooved Feed: Hot temperature: 120°C (212°F) |
| Тип материала | Категория | Производитель |
|---|---|---|
| TOPAS® 6017S-04 | COC | Topas Advanced Polymers, Inc. |
| TOPAS® 8007F-500 | COC | Polyplastics Co., Ltd. |
| TOPAS® 8007F-600 | COC | Topas Advanced Polymers, Inc. |
| TOPAS® 8007X-10 | COC | Topas Advanced Polymers, Inc. |
| TOPAS® 8007F-04 | COC | Topas Advanced Polymers, Inc. |
| TOPAS® IT X1 | COC | Topas Advanced Polymers, Inc. |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved