Описание материалов:
AvaSpire AV-621 CF30 is a AvaSpire AV-621 30% carbon fiber reinforced brand. Dimensional stability and warpage resistance are better than those of 30% carbon fiber reinforced PEEK. Toughness and impact strength are higher than PEEK (polyetheretherketone). Among all AV 621 grades, AV-621 CF30 has the highest strength, rigidity and fatigue resistance. Moreover, the resin also retains most of the useful key properties of carbon fiber reinforced PEEK, including chemical resistance, fatigue resistance, and long-term thermal oxidation stability. The excellent balance of various properties of the AV-621 CF30 enables it to be used for a wide range of purposes in all walks of life, including healthcare, transportation, electronics and chemical processing.
The material can be easily melted on standard equipment. The melt processability of AV-621 CF30 is very close to that of 30% CF-enhanced PEEK. The low fluidity AV-621 CF30 brand is very suitable for extrusion purposes and has the properties of AV-651 CF30.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Армированный углеродным волокном материал, 30% наполнитель по весу
|
| Характеристики | - Хорошая стабильность размеров
- Жесткий, высокий
- Высокая прочность
- Хорошая химическая стойкость
- Сопротивление усталости
- Теплостойкость, высокая
- Огнестойкий
|
| Используется | - Детали Насоса
- Уплотнение
- Медицинские принадлежности/принадлежности для ухода
|
| Соответствие RoHS | - Свяжитесь с производителем
|
| Внешний вид | |
| Формы | |
| Метод обработки | - Машинная обработка
- Экструзионное формование профиля
- Литье под давлением
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.42 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (400°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Формовочная усадка 1 | | | ASTM D955 |
| Flow
: 3.18mm | 0.0 - 0.20 | % | ASTM D955 |
| Transverse flow
: 3.18mm | 0.90 - 1.1 | % | ASTM D955 |
| Поглощение воды (24 hr) | 0.10 | % | ASTM D570 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (M-Scale) | 101 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | | | |
| -- 2 | 17200 | MPa | ASTM D638 |
| -- | 23300 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | | | |
| Yield | 196 | MPa | ISO 527-2/1A/5 |
| -- 3 | 181 | MPa | ASTM D638 |
| Удлинение при растяжении | | | |
| Fracture 4 | 2.2 | % | ASTM D638 |
| Fracture | 2.2 | % | ISO 527-2/1A/5 |
| Флекторный модуль | | | |
| -- | 15100 | MPa | ASTM D790 |
| -- | 21300 | MPa | ISO 178 |
| Flexural Strength | | | |
| -- | 276 | MPa | ASTM D790 |
| -- | 296 | MPa | ISO 178 |
| Прочность на сжатие | 152 | MPa | ASTM D695 |
| Прочность сдвига | 91.0 | MPa | ASTM D732 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | | | |
| -- | 69 | J/m | ASTM D256 |
| -- | 9.6 | kJ/m² | ISO 180 |
| Незубчатый изод Impact | | | |
| -- | 640 | J/m | ASTM D4812 |
| -- | 39 | kJ/m² | ISO 180 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке 5(1.8 MPa, Annealed, 3.20 mm) | 210 | °C | ASTM D648 |
| Температура перехода стекла | 160 | °C | ASTM D3418 |
| Пиковая температура плавления | 340 | °C | ASTM D3418 |
| CLTE-
Поток (-50 to 50°C) | 5.0E-6 | cm/cm/°C | ASTM E831 |
| Удельный нагрев | | | DSC |
| 50°C | 1350 | J/kg/°C | DSC |
| 200°C | 1810 | J/kg/°C | DSC |
| Теплопроводность | 0.35 | W/m/K | ASTM E1530 |
| Анализ заполнения | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Melt Viscosity (400°C, 1000 sec^-1) | 790 | Pa·s | ASTM D3835 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 149 | °C | |
| Время сушки | 4.0 | hr | |
| Задняя температура | 366 | °C | |
| Средняя температура | 371 | °C | |
| Передняя температура | 377 | °C | |
| Температура сопла | 382 | °C | |
| Температура обработки (расплава) | 366 - 388 | °C | |
| Температура формы | 149 - 177 | °C | |
| Скорость впрыска | Fast | | |
| Коэффициент сжатия винта | 2.0 : 1.0 - 3.0 : 1.0 | | |
| Инструкции по впрыску |
|---|
| 保压压力：最低值 |
| Примечание |
|---|
| 1 . | 5" x 0.5" x 0.125" bars |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 200°C,2 hours |