Escor™ 6000

Категория	EAA, Ethylene Acrylic Acid Copolymer Resin
Производитель	ExxonMobil Chemical
Торговая марка	Escor™
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	OkS6Hd_Escor-6000.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

Escor 6000 is mainly used for extrusion coating and coextrusion coating. Escor 6000 is a high drafting product form of Escor 5000. Very low coating weight can be achieved at high production line speeds. It can be well bonded to polar substrates, aluminum foils, metal films, paper, steel and glass surfaces. Provides an excellent balance of adhesion to the substrate surface and interlaminar binding force with coextruded low-density polyethylene and ethylene vinyl acetate

Главная Информация

Физический	Номинальное значение	Единица измерения	Метод испытания
Массовый расход расплава (MFR) (190°C/2.16 kg)	8.2	g/10 min	ASTM D1238
Содержание акриловой кислоты	6.0	wt%	ExxonMobil Method

Юридическое заявление
有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用

Инструкции по экструзии
Excellent results are obtained in extrusion coating at 260°C - 280°C (500°F - 536°F) temperature range. Processing temperatures above 300°C (572°F) may cause resin degradation. To minimize corrosion risk, all exposed metal surfaces in the extruder and die should be made from corrosion resistant metals or nickel/chrome plated. ESCOR should be fed into the extruder after LDPE of a similar or higher melt index. Machines should always be completely purged with LDPE or a suitable cleaning compound before shutdown.

Инструкции по экструзии

Excellent results are obtained in extrusion coating at 260°C - 280°C (500°F - 536°F) temperature range. Processing temperatures above 300°C (572°F) may cause resin degradation. To minimize corrosion risk, all exposed metal surfaces in the extruder and die should be made from corrosion resistant metals or nickel/chrome plated. ESCOR should be fed into the extruder after LDPE of a similar or higher melt index. Machines should always be completely purged with LDPE or a suitable cleaning compound before shutdown.

Тип материала	Категория	Производитель
Escor™ 5070	EAA	ExxonMobil Chemical
E-FLEX™ I3265	EAA	Mando Advanced Materials Co., Ltd.
PRIMACOR™ 3003	EAA	The Dow Chemical Company
PRIMACOR™ 3330	EAA	The Dow Chemical Company
PRIMACOR™ 1430	EAA	The Dow Chemical Company
Bynel® 2022	EAA	DuPont Packaging & Industrial Polymers

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

