EOS PA 2241 FR
| Категория | PA12, Polyamide 12 , Nylon 12 |
| Производитель | EOS GmbH |
| Торговая марка | EOS |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
ApWHxU_EOS-PA-2241-FR.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Product information
PA 2241 FR is a flame retardant polyamide 12 for processing in laser sintering systems. It contains a halogen-based flame retardant. Mainly due to its recyclability the material is economical, enabling low-cost part production.
Properties
Acceptance criteria
Typical applications
PA 2241 FR is a flame retardant polyamide 12 for processing in laser sintering systems. It contains a halogen-based flame retardant. Mainly due to its recyclability the material is economical, enabling low-cost part production.
Properties
- flame retardant
- economic
- high strain at tensile strength
Acceptance criteria
- JAR 25 (aviation)
Typical applications
- aviation (interior, e.g. air ducts and air outlet valves)
| Главная Информация | |
|---|---|
| Добавка |
|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Внешний вид |
|
| Формы |
|
| Метод обработки |
|
| Физический | Сухой | Состояние | Единица измерения | Метод испытания |
|---|---|---|---|---|
| Плотность | 1.00 | -- | g/cm³ | Internal Method |
| Видимая плотность | 0.45 | -- | g/cm³ | ISO 60 |
| Механические | Сухой | Состояние | Единица измерения | Метод испытания |
|---|---|---|---|---|
| Модуль растяжения 1 | 1900 | 1600 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| 6.0% Strain 2 | 46.0 | -- | MPa | ISO 527-2 |
| 7.0% Strain 3 | 49.0 | -- | MPa | ISO 527-2 |
| 8.0% Strain 4 | -- | 41.0 | MPa | ISO 527-2 |
| 11% Strain 5 | -- | 44.0 | MPa | ISO 527-2 |
| Растяжимое напряжение | ||||
| Break 6 | 6.0 | 9.0 | % | ISO 527-2 |
| Break 7 | 15 | 22 | % | ISO 527-2 |
| Тепловой | Сухой | Состояние | Единица измерения | Метод испытания |
|---|---|---|---|---|
| Heat Deflection Temperature 8 | ||||
| 0.45 MPa, Unannealed | 154 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 84.0 | -- | °C | ISO 75-2/A |
| Температура плавления 9 | 185 | -- | °C | ISO 11357 |
| Воспламеняемость | Сухой | Состояние | Метод испытания | |
|---|---|---|---|---|
| Испытание пламени | FAR 25.853 | |||
| 12s Ignition Time : 1.00 mm | Passed | -- | ||
| 12s Ignition Time : 1.50 mm | Passed | -- | ||
| 12s Ignition Time : 2.00 mm | Passed | -- | ||
| 60s Ignition Time : 1.00 mm | Passed | -- | ||
| 60s Ignition Time : 1.50 mm | Passed | -- | ||
| 60s Ignition Time : 2.00 mm | Passed | -- | ||
| Плотность Дыма | AITM 2.0007 | |||
| 1.00 mm | Passed | -- | ||
| 1.50 mm | Passed | -- | ||
| 2.00 mm | Passed | -- | ||
| Токсичность | AITM 3.0005 | |||
| 1.00 mm | Passed | -- | ||
| 1.50 mm | Passed | -- | ||
| 2.00 mm | Passed | -- |
| Примечание | |
|---|---|
| 1 . | Z Direction |
| 2 . | Z Direction |
| 3 . | X Direction |
| 4 . | Z Direction |
| 5 . | X Direction |
| 6 . | Z Direction |
| 7 . | Y Direction |
| 8 . | X Direction |
| 9 . | 20°C/min |
| Тип материала | Категория | Производитель |
|---|---|---|
| Rilsamid® AMN Noir T6LD | Nylon 12 | Arkema |
| LUVOCOM® 6-8395 | Nylon 12 | Lehmann & Voss & Co. |
| LNP™ LUBRICOMP™ SP003 compound | Nylon 12 | SABIC Innovative Plastics |
| LNP™ LUBRICOMP™ SFP36 compound | Nylon 12 | SABIC Innovative Plastics |
| Latimass 82-02 D030 | Nylon 12 | LATI S.p.A. |
| Grilamid® LV-3 ESD | Nylon 12 | EMS-GRIVORY |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved