LUVOCOM庐 6-8438-1

Категория	PA12, Polyamide 12 , Nylon 12
Производитель	Lehmann & Voss & Co.
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	i7XcsC_LUVOCOM-6-8438-1.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®6-8438-1 is a polyamide 12 (nylon 12) material, and the filler is glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main characteristics of 6-8438-1 are: moisture resistance.

Typical application areas include:

engineering/industrial accessories

House

textile/fiber

Automotive Industry

business/office supplies

Главная Информация
Наполнитель/армирование	Армированный стекловолокном материал
Характеристики	Быстрый статический спад Низкий или не впитывающий
Используется	Ручка Текстильные изделия Инженерные аксессуары Ролик Применение в автомобильной области Бизнес-оборудование Чехол
Внешний вид	Серый

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.22	g/cm³	ISO 1183
Формовочная усадка	0.30 - 0.60	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.10	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	4000	MPa	ISO 527-2
Tensile Stress (Break)	65.0	MPa	ISO 527-2
Растяжимое напряжение (Yield)	3.5	%	ISO 527-2
Флекторный модуль	3500	MPa	ISO 178
Флекторный стресс	96.0	MPa	ISO 178
Flexural Strain at Flexural Strength	4.6	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	140	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	1.0E+9	ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Charpy Unnotched Impact Strength (23°C)	48	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Температура непрерывного использования	90.0	°C	UL 746B

Электрический	Номинальное значение	Единица измерения	Метод испытания
Удельное сопротивление поверхности	> 1.0E+9	ohms	IEC 60093

Инъекция	Номинальное значение	Единица измерения
Температура сушки
A	75.0	°C
B	105	°C
Время сушки- A	6.0 - 10	hr
Рекомендуемая максимальная влажность	0.10	%
Задняя температура	230 - 250	°C
Средняя температура	240 - 260	°C
Передняя температура	250 - 270	°C
Температура сопла	250 - 260	°C
Температура обработки (расплава)	250	°C
Температура формы	70.0 - 110	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Тип материала	Категория	Производитель
Rilsan® AESN P10 TL	Nylon 12	Arkema
RTP 200F MS 2	Nylon 12	RTP Company
UBESTA 3030 JFX3	Nylon 12	UBE Engineering Plastics, S.A.
RTP 285 F TFE 13 SI 2	Nylon 12	RTP Company
Generic Nylon 12 - Carbon Fiber	Nylon 12	Generic
Latimass 82-03 D110	Nylon 12	LATI S.p.A.

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

