DuraSurf™ BSR
| Категория | UHMWPE, Ultra High Molecular Weight Polyethylene |
| Производитель | Crown Plastics |
| Торговая марка | DuraSurf™ |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
AW9G5X_DuraSurf-BSR.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Crown Plastics DuraSurf™ BSR tapes are specifically designed to meet the demands of the automotive industry to help eliminate Buzz, Squeak and Rattle issues with auto interiors. DuraSurf™ BSR helps eliminate wear and noise between dissimilar materials, eliminate warranty issues, allow movement in adjoining parts, protect painted surfaces, reduce marring, help extend vehicle life, is easily die-cuttable and can fit into existing designs. The DuraSurf™ BSR tapes are tested to all of the major automotive specifications including GM9985804, GM6419M, Ford ESB-M3G123-B and Chrysler MS-CH612.
AVAILABLE THICKNESS
.005" (.125 mm), .010" (.25 mm), .015" (.38 mm), .020" (.5 mm)
AVAILABLE WIDTHS
All dimensions between 1/4" (6.35 mm) and 24" (610 mm)
UHMW PROPERTIES
AVAILABLE THICKNESS
.005" (.125 mm), .010" (.25 mm), .015" (.38 mm), .020" (.5 mm)
AVAILABLE WIDTHS
All dimensions between 1/4" (6.35 mm) and 24" (610 mm)
UHMW PROPERTIES
- Excellent abrasion and wear resistance
- Very high impact strength
- Meets FDA and USDA guidelines
- No moisture absorption
- Self-lubricating - no need for oils or lubricants
- Excellent noise abatement properties
- Chemical resistance and corrosion resistant
- Maintains performance and properties at -30°C
- Meets ASTM-D-4020-81
- Low coefficient of friction
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес 1 | 0.930 | g/cm³ | ASTM D792 |
| Crystallinity | ASTM D3417 | ||
| 762.0 µm | 48 | % | |
| 1.52 mm | 47 | % | |
| 3.18 mm | 50 | % | |
| Relative Viscosity | ASTM D4020 | ||
| 762.0 µm | 230 to 350 | cm³/g | |
| 1.52 mm | 230 to 350 | cm³/g | |
| 3.18 mm | 230 to 350 | cm³/g |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Static Decay | |||
| 762.0 µm | < 10 | msec | |
| 1.52 mm | < 10 | msec | |
| 3.18 mm | < 10 | msec |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Твердость дюрометра | ASTM D2240 | ||
| Shore D, 0.762 mm | 65 | ||
| Shore D, 1.52 mm | 65 | ||
| Shore D, 3.18 mm | 65 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Модуль растяжения | ASTM D638 | ||
| 0.762 mm | 725 | MPa | |
| 1.52 mm | 731 | MPa | |
| 3.18 mm | 672 | MPa | |
| Прочность на растяжение | ASTM D638 | ||
| Yield, 0.762 mm | 23.0 | MPa | |
| Yield, 1.52 mm | 20.0 | MPa | |
| Yield, 3.18 mm | 22.0 | MPa | |
| Break, 0.762 mm | 53.0 | MPa | |
| Break, 1.52 mm | 49.0 | MPa | |
| Break, 3.18 mm | 44.0 | MPa | |
| Удлинение при растяжении | ASTM D638 | ||
| Break, 0.762 mm | 60 | % | |
| Break, 1.52 mm | 460 | % | |
| Break, 3.18 mm | 470 | % | |
| Коэффициент трения | ASTM D1894 | ||
| vs. Itself - Dynamic 2 | 0.14 | ||
| vs. Itself - Dynamic 3 | 0.14 | ||
| vs. Itself - Dynamic 4 | 0.13 | ||
| vs. Itself - Static 5 | 0.16 | ||
| vs. Itself - Static 6 | 0.16 | ||
| vs. Itself - Static 7 | 0.16 | ||
| vs. Steel - Dynamic 8 | 0.050 to 0.080 | ||
| vs. Steel - Dynamic 9 | 0.050 to 0.10 | ||
| vs. Steel - Dynamic 10 | 0.10 to 0.22 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Зубчатый изод Impact 11(3.18 mm) | 80 | J/m | ASTM D256 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Пиковая температура плавления | |||
| -- 12 | 134 | °C | |
| -- 13 | 136 | °C | |
| CLTE- Поток | ASTM D696 | ||
| -100 to -20°C, 3.18 mm | 9.2E-4 | cm/cm/°C | |
| 20 to 100°C, 3.18 mm | 1.5E-4 | cm/cm/°C |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельное сопротивление поверхности | ASTM D257 | ||
| 0.762 mm | 1.0E+3 | ohms | |
| 1.52 mm | 1.0E+3 | ohms | |
| 3.18 mm | 1.0E+3 | ohms | |
| Сопротивление громкости | ASTM D257 | ||
| 0.762 mm | 6.0E+7 | ohms·cm | |
| 1.52 mm | 1.5E+7 | ohms·cm | |
| 3.18 mm | > 2.0E+7 | ohms·cm | |
| Диэлектрическая прочность (3.18 mm) | 14 | kV/mm | ASTM D149 |
| Диэлектрическая постоянная | ASTM D150 | ||
| 0.762 mm | 2.39 | ||
| 1.52 mm | 2.29 | ||
| 3.18 mm | 2.28 | ||
| Коэффициент рассеивания | ASTM D150 | ||
| 0.762 mm, 10 kHz | -1.0E-3 | ||
| 0.762 mm, 5 MHz | -1.0E-3 | ||
| 1.52 mm, 10 kHz | -2.0E-3 | ||
| 1.52 mm, 5 MHz | -1.0E-3 | ||
| 3.18 mm, 10 kHz | 0.0 | ||
| 3.18 mm, 5 MHz | -1.0E-3 |
| Примечание | |
|---|---|
| 1 . | 0.125 inches |
| 2 . | 0.03 inches |
| 3 . | 0.125 inches |
| 4 . | 0.06 inches |
| 5 . | 0.03 inches |
| 6 . | 0.06 inches |
| 7 . | 0.125 inches |
| 8 . | Oil |
| 9 . | Water |
| 10 . | Dry |
| 11 . | 5.0 mm Notch Depth |
| 12 . | 0.125 inches |
| 13 . | 0.03 inches |
| Тип материала | Категория | Производитель |
|---|---|---|
| Avalon 37 | UHMWPE | Greene, Tweed & Co. |
| Quadrant EPP TIVAR® 1000 ESD | UHMWPE | Quadrant Engineering Plastic Products |
| POLYSTONE® MR | UHMWPE | Röchling Engineering Plastics SE & Co. KG |
| Quadrant EPP CESTILENE HD 1000 R | UHMWPE | Quadrant Engineering Plastic Products |
| UTEC 6540 | UHMWPE | Braskem |
| DeWAL DW 401 | UHMWPE | DeWAL Industries |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved