Описание материалов:
Eastar™ A150 Copolyester is a poly(1,4-cyclohexylene-dimethylene terephthalate/isophthalate). It is produced by reacting terephthalic acid and isophthalic acid with the glycol 1,4-cyclohexanedimethanol. Eastar™ A150 is intended primarily for extrusion into film and sheeting for packaging applications. It has excellent hydrolytic stability and good heat stability. Eastar™ A150 copolyester is lawful for use in food contact applications under food additive regulations published at 21 CFR 177.1240 by the Federal Food and Drug Administration. Therefore, it is lawful for use as a packaging material for meat or poultry foods prepared under federal inspection of the U.S. Department of Agriculture regulations at 9 CFR 318.7 and 381.147.
This product has been GREENGUARD INDOOR AIR QUALITY CERTIFIED®.
The GREENGUARD INDOOR AIR QUALITY CERTIFIED® Mark is a registered certification mark used under license through the GREENGUARD Environmental Institute (GEI). GEI is an industry-independent, non-profit organization that oversees the GREENGUARD Certification Program. The GREENGUARD Certification Program is an industry independent, third-party testing program for low-emitting products and materials for indoor environments. For more information about GEI and to obtain printable certificates for Eastman™ Copolyesters, visit www.greenguard.org. Choose Eastman Chemical Company under the Manufacturer category and click search to display a list of our products.
| Главная Информация | |
|---|
| Характеристики | - Приемлемый пищевой контакт
- Гидролитически стабильный
|
| Используется | - Пленка
- Пищевая упаковка
- Неспецифические пищевые приложения
- Упаковка
|
| Рейтинг агентства | - Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 177,1240
- USDA 9 CFR 318,7
- USDA 9 CFR 381,147
|
| Формы | |
| Метод обработки | - Экструзионная пленка
- Экструзионный лист
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность 1 | 1.20 | g/cm³ | ASTM D1505 |
| Видимая плотность | | | ASTM D1895 |
| Poured | 0.67 | g/cm³ | |
| Vibrated | 0.73 | g/cm³ | |
| Внутренняя вязкость | | | Internal Method |
| 23°C 2 | 0.77 | | |
| 23°C, 280.0 µm 3 | 0.73 | | |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Проницаемость диоксида углерода (23 °C) | 59 | cm³·mm/m²/atm/24 hr | ASTM D1434 |
| Сопротивление размножению разрыва 4 | | | ASTM D1938 |
| MD
: 23°C, 280.0 µm | 19 | kN/m | |
| TD
: 23°C, 280.0 µm | 18 | kN/m | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Тепло плавления (23 °C) 5 | 32.0 | kJ/kg | ASTM E793 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Коэффициент трения | 0.60 | | ASTM D1894 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 280 | µm | |
| Сектантный модуль | | | ASTM D882 |
| MD
: 280 µm | 1600 | MPa | |
| TD
: 280 µm | 1600 | MPa | |
| Прочность на растяжение | | | ASTM D882 |
| MD
: Yield, 280 µm | 43.0 | MPa | |
| TD
: Yield, 280 µm | 43.0 | MPa | |
| MD
: Break, 280 µm | 56.0 | MPa | |
| TD
: Break, 280 µm | 56.0 | MPa | |
| Удлинение при растяжении | | | ASTM D882 |
| MD
: Yield, 280 µm | 5.0 | % | |
| TD
: Yield, 280 µm | 5.0 | % | |
| MD
: Break, 280 µm | 250 | % | |
| TD
: Break, 280 µm | 250 | % | |
| Ударное падение Dart 6 | | | ASTM D1709A |
| -30°C, 280 µm | 710 | g | |
| -18°C, 280 µm | 750 | g | |
| 23°C, 280 µm | 680 | g | |
| Elmendorf Tear Strength | | | ASTM D1922 |
| MD
: 280 µm | 1600 | g | |
| TD
: 280 µm | 1700 | g | |
| Проницаемость кислорода (23°C, 280 µm, 50% RH) | 13 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Скорость передачи водяного пара (38°C, 100% RH, 280 µm) | 5.0 | g/m²/24 hr | ASTM F372 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура перехода стекла 7 | 91.0 | °C | ASTM D3418 |
| Пиковая температура плавления 8 | 261 | °C | ASTM D3418 |
| Удельный нагрев 9 | | | |
| 23°C | 1200 | J/kg/°C | DSC |
| 80°C | 1400 | J/kg/°C | DSC |
| 100°C | 1700 | J/kg/°C | DMTA |
| 200°C | 1900 | J/kg/°C | DSC |
| 280°C | 2200 | J/kg/°C | DSC |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск (45°, 280 µm) | 108 | | ASTM D2457 |
| Коэффициент пропускания | | | ASTM D1003 |
| Total, 280 µm | 93.0 | % | |
| Regular, 280 µm | 90.0 | % | |
| Четкость (280 µm) | 85.0 | | ASTM D1746 |
| Haze (280 µm) | 0.50 | % | ASTM D1003 |
| Примечание |
|---|
| 1 . | Film, 280 µm |
| 2 . | EMN-A-AC-G-V-1 |
| 3 . | Film, EMN-A-AC-G-V-1 |
| 4 . | Split Tear Method, 254 mm/min |
| 5 . | Determined by DSC on the first heating cycle. |
| 6 . | 12.7 mm dia. head, 127 mm dia. clamp, 600 mm drop |
| 7 . | Determined by DSC on the 2nd heating cycle. |
| 8 . | Determined by DSC on the 2nd heating cycle. |
| 9 . | Determined by DSC on the first heating cycle. |