Описание материалов:
Eastman Embrace™ High Yield is combined with Eastman Embrace™ LV copolyester to create a white opaque microvoided shrinkable film. Embrace High Yield has a density below 1.0 g/cc with a high ultimate shrinkage up to 70%. Benefits of Embrace High Yield such as UV and visible light protection, and optimum MD growth that is ~30% less dense than other copolyesters, enabling more film per weight, offer a robust packaging solution that is appealing to the consumer and functionable for the brand owner. Unique shelf appeal, marketing benefits of full body shrink film labels along with the ability to shrink around highly contoured containers makes Eastman Embrace HY™ copolyester another new and fresh idea from Eastman Chemical Company that will further differentiate your product.
This product has been GREENGUARD INDOOR AIR QUALITY CERTIFIED®.
The GREENGUARD INDOOR AIR QUALITY CERTIFIED® Mark is a registered certification mark used under license through the GREENGUARD Environmental Institute (GEI). GEI is an industry-independent, non-profit organization that oversees the GREENGUARD Certification Program. The GREENGUARD Certification Program is an industry independent, third-party testing program for low-emitting products and materials for indoor environments. For more information about GEI and to obtain printable certificates for Eastman™ Copolyesters, visit www.greenguard.org. Choose Eastman Chemical Company under the Manufacturer category and click search to display a list of our products.
| Главная Информация | |
|---|
| Характеристики | - Отличная Печатающая способность
- Хорошая устойчивость к ультрафиолетовому излучению
- Высокая усадка
- Низкая плотность
- Мягкий
|
| Используется | - Косметическая упаковка
- Пленка
- Пищевая упаковка
- Этикетки
- Упаковка
- Фармацевтическая упаковка
- Термоусадочная пленка
|
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.890 | g/cm³ | ASTM D1505 |
| Цвет 1 | | | ASTM E1331 |
| a | -0.17 | | |
| b | -0.26 | | |
| L | 93 | | |
| Opacity | 91 | | |
| Усадка 2 | | | Internal Method |
| MD
: 95°C | -1.0 | % | |
| TD
: 95°C | 73 | % | |
| Поверхностное натяжение 3 | | | Internal Method |
| Harmonic Mean, Dispersive
: 23°C | 36 | mN/m | |
| Harmonic Mean, Total
: 23°C | 36 | mN/m | |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Проницаемость углекислого газа (30 °C, 63,5 мкм) 4 | 43 | cm³·mm/m²/atm/24 hr | ASTM D1434 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| UV Transmittance 5 | | | |
| 300 nm | 0.20 | % | |
| 325 nm | 6.0 | % | |
| 350 nm | 9.8 | % | |
| 375 nm | 12 | % | |
| 400 nm | 13 | % | |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 64 | µm | |
| Сектантный модуль | | | ASTM D882 |
| MD
: 64 µm | 850 | MPa | |
| TD
: 64 µm | 3000 | MPa | |
| Прочность на растяжение | | | ASTM D882 |
| MD
: Break, 64 µm | 23.0 | MPa | |
| TD
: Break, 64 µm | 117 | MPa | |
| Удлинение при растяжении | | | ASTM D882 |
| MD
: Break, 64 µm | 380 | % | |
| TD
: Break, 64 µm | 22 | % | |
| Проницаемость кислорода (30°C, 64 µm, 68% RH) | 10 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Скорость передачи водяного пара (38°C, 100% RH, 64 µm) | 38 | g/m²/24 hr | ASTM F1249 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура перехода стекла 6 | 77.0 | °C | Internal Method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск (60°, 63.5 µm) | 8 | | ASTM D2457 |
| Yellowness Index (63.5 mm) | 1.7 | YI | ASTM E313 |
| Примечание |
|---|
| 1 . | CIELAB, D65, 10° |
| 2 . | 10 sec |
| 3 . | ECRL-A-PA-G-TEN-3-2 |
| 4 . | 68% RH |
| 5 . | Integrating sphere, Embrace Copolyester + 25% High Yield HY1000 Compound |
| 6 . | EMNR-A-AS-G-DTP-1-1, 2nd heating scan |