Описание материалов:
LDJ226 is a low density polyethylene designed predominantly for use in bundle shrink film and a variety of low gauge (20 - 50µm) general purpose applications where a medium slip film is required. LDJ226 is formulated with a process stabilisation and antiblock package and contains antistatic additives.
LDJ226 is intended for use in a wide range of shrink and general purpose film applications typically of the thickness 20 to 50µm.
LDJ226 is intended for use in a wide range of shrink and general purpose film applications typically of the thickness 20 to 50µm.
| Главная Информация | |
|---|---|
| Добавка |
|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.922 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 32 | µm | |
| Сектантный модуль | ASTM D882 | ||
| 2% secant, MD : 32 µm, blown film | 160 | MPa | ASTM D882 |
| 2% secant, TD : 32 µm, blown film | 190 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 32 µm, blown film | 11.0 | MPa | ASTM D882 |
| TD : Yield, 32 µm, blown film | 10.0 | MPa | ASTM D882 |
| MD : Broken, 32 µm, blown film | 22.0 | MPa | ASTM D882 |
| TD : Broken, 32 µm, blown film | 16.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Broken, 32 µm, blown film | 270 | % | ASTM D882 |
| TD : Broken, 32 µm, blown film | 740 | % | ASTM D882 |
| Ударное падение Dart (32 µm, Blown Film) | 70 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 32 µm, blown film | 390 | g | ASTM D1922 |
| TD : 32 µm, blown film | 170 | g | ASTM D1922 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45 °, 32.0 µm, blown film) | 71 | ASTM D2457 | |
| Haze (32.0 µm, blown film) | 7.0 | % | ASTM D1003 |
| Дополнительная информация |
|---|
| Film properties taken from blown film processed at a blow up ratio of 2:1. |
| Тип материала | Категория | Производитель |
|---|---|---|
| NEXUS PE LLDPE-H118 | LLDPE | Nexus Resin Group, LLC. |
| FINGERPRINT™ DFDA-7510 NT | LLDPE | The Dow Chemical Company |
| HANWHA LLDPE 9730 | LLDPE | Hanwha Chemical |
| Jam PE 30505 | LLDPE | Jam Petrochemical Company |
| Lotrène® LLDPE Q2018H | LLDPE | QATOFIN Company Limited |
| Braskem PE SLH118 | LLDPE | Braskem |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved