Описание материалов:
Lustran ABS 488 resin is a general-purpose injection molding grade of ABS (acrylonitrile butadiene styrene). It is a medium-to-high impact ABS with very high gloss. In addition to a good balance of physical properties, it provides very good moldability and improved surface aesthetics versus Lustran ABS 448.
Lustran ABS 488 is used in applications requiring greater toughness than Lustran ABS 248 and better aesthetics than Lustran ABS 448. It is used in home appliances (vacuum cleaners); musical equipment; and office products requiring high gloss, such as keyboard keys and pen barrels. It is also used in swimming pool filter pump housings. Per the restrictions of the Consumer Product Safety Improvement Act (CPSIA) that went into effect on February 10, 2009, Lustran ABS 488 can not be used to manufacture children's toys or child care articles. As with any product, use of Lustran ABS 488 resin in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.
Главная Информация | |
---|
Характеристики | - Подсветка
- Хорошая производительность формования
- Хорошая прочность
- Универсальный
- Отличный внешний вид
- Средняя ударопрочность
|
Используется | - Электроприборы
- Музыкальный инструмент
- Бизнес-оборудование
- Чехол
- Канцелярские принадлежности
|
Рейтинг агентства | |
Формы | |
Метод обработки | |
Многоточечные данные | - Изоляционный стресс против деформации (ISO 11403-1)
- Сектантный модуль против деформации (ISO 11403-1)
|
Физический | Номинальное значение | Единица измерения | Метод испытания |
---|
Удельный вес | 1.05 | g/cm³ | ASTM D792 |
Удельный объем | 0.950 | cm³/g | ASTM D792 |
Массовый расход расплава (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
Формовочная усадка-
Поток | 0.40 - 0.60 | % | ASTM D955 |
Твердость | Номинальное значение | Единица измерения | Метод испытания |
---|
Твердость Роквелла (R-Scale) | 105 | | ASTM D785 |
Механические | Номинальное значение | Единица измерения | Метод испытания |
---|
Модуль растяжения | 2520 | MPa | ASTM D638 |
Прочность на растяжение (Yield) | 42.1 | MPa | ASTM D638 |
Флекторный модуль | 2550 | MPa | ASTM D790 |
Flexural Strength (Yield) | 70.3 | MPa | ASTM D790 |
Воздействие | Номинальное значение | Единица измерения | Метод испытания |
---|
Зубчатый изод Impact | | | ASTM D256 |
-40°C, 3.18 mm | 59 | J/m | ASTM D256 |
23°C, 3.18 mm | 290 | J/m | ASTM D256 |
Тепловой | Номинальное значение | Единица измерения | Метод испытания |
---|
Температура отклонения при нагрузке | | | ASTM D648 |
0.45 MPa, not annealed | 95.0 | °C | ASTM D648 |
1.8 MPa, not annealed | 84.4 | °C | ASTM D648 |
Викат Температура размягчения | 101 | °C | ASTM D1525 1 |
CLTE-
Поток | 9.0E-5 | cm/cm/°C | ASTM D696 |
RTI Elec (1.57 mm) | 60.0 | °C | UL 746 |
RTI Imp (1.57 mm) | 60.0 | °C | UL 746 |
RTI Str (0.157 mm) | 60.0 | °C | UL 746 |
Воспламеняемость | Номинальное значение | | Метод испытания |
---|
Огнестойкость | | | UL 94 |
1.59 mm | HB | | UL 94 |
3.30 mm | HB | | UL 94 |
Инъекция | Номинальное значение | Единица измерения | |
---|
Температура сушки | | | |
A | 82.2 - 87.8 | °C | |
B | 71.1 - 76.7 | °C | |
Время сушки | | | |
A | 2.0 | hr | |
B | 4.0 | hr | |
Рекомендуемая максимальная влажность | < 0.10 | % | |
Рекомендуемый размер снимка | 50 - 75 | % | |
Рекомендуемый Макс измельчения | 20 | % | |
Задняя температура | 235 - 249 | °C | |
Средняя температура | 241 - 254 | °C | |
Передняя температура | 246 - 260 | °C | |
Температура сопла | 246 - 260 | °C | |
Температура обработки (расплава) | 246 - 260 | °C | |
Температура формы | 43.3 - 65.6 | °C | |
Давление впрыска | 68.9 - 110 | MPa | |
Скорость впрыска | Fast | | |
Back Pressure | 0.00 - 0.172 | MPa | |
Тонаж зажима | 2.8 - 5.5 | kN/cm² | |
Подушка | < 6.35 | mm | |
Отношение винта L/D | 20.0:1.0 | | |
Коэффициент сжатия винта | 2.5:1.0 | | |
Инструкции по впрыску |
---|
Hold Pressure: 50 to 75% of Injection PressureScrew Speed: Moderate |
Примечание |
---|
1 . | 标准 B (120°C/h) |