Описание материалов:
Baydur GS-772 is a solid polyurethane system used in the reaction injection molding (RIM) process. The system is supplied as two reactive liquid components. Component A is a polymetric diphenylmethane diisocyanate (PMDI) and component B is a formulated polyol system.
Baydur GS-772 system is used in applications where harsh environmental conditions are encountered, such as pump housings, catch basins, and underground equipment. It is also used as a replacement for cast iron where the application requires weight reduction, improved corrosion resistance, and/or improved abrasion resistance. As with and product, use of the Baydur GS-772 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Характеристики | - Хорошая коррозионная стойкость
- Хорошая стойкость к истиранию
|
| Используется | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | | | |
| -- | 0.708 | g/cm³ | ASTM D1622 |
| -- | 1.13 | g/cm³ | ASTM D792 |
| Формовочная усадка-
Поток | 1.0 - 1.2 | % | Internal method |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore D) | 76 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение (Break) | 39.3 | MPa | ASTM D638 |
| Удлинение при растяжении (Break) | 10 | % | ASTM D638 |
| Флекторный модуль | 1380 | MPa | ASTM D790 |
| Flexural Strength | 60.0 | MPa | ASTM D790 |
| Прочность на сжатие | 34.5 | MPa | ASTM D695 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 6400 | µm | |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | 48 | J/m | ASTM D256 |
| Незубчатый изод Impact | 370 | J/m | ASTM D256 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке (0.45 MPa, Unannealed) | 98.9 | °C | ASTM D648 |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость | V-0 | | UL 94 |
| Термокомплект | Номинальное значение | | |
|---|
| Компоненты термокомплекта | | | |
| Component a | Mixing ratio calculated by weight: 100, mixing ratio calculated by capacity: 86 | | |
| Component B | Mixing ratio by weight: 100, mixing ratio by capacity: 100 | | |
| Дополнительная информация |
|---|
| Part A
Type: Isocyanate
Appearance: Dark brown liquid
Specific Gravity @ 25°C: 1.24
Viscosity @ 25°C: 200 mPa*s
Flash Point PMCC: 199°C
NCO: 31.0 min wt%
Part B
Type: Polyol
Appearance: Black liquid
Specific Gravity @ 25°C: 1.05
Viscosity @ 25°C: 1700 mPa*s
Flash Point PMCC: 206°C
Water: 0.08 wt%
Hydroxyl Number: 370 mg KOH/g
Material Temperature: 32 to 38°CMold Temperature: 60 to 71°CMachine Reactive @ 35°C: 16 secTypical Cure Time: 3 to 6 minTypical Mold Density: 65 to 71 lb/ft³ |
| Тип материала |
Категория |
Производитель |
|
Xuchuan XCS-4575 |
PUR, Unspecified |
Xuchuan Chemical (Suzhou) Co., Ltd
|
|
Xuchuan XCM-18S |
PUR, Unspecified |
Xuchuan Chemical (Suzhou) Co., Ltd
|
|
Ebalta MG 453 / Comp. A+B |
PUR, Unspecified |
Ebalta Kunststoff GmbH
|
|
Epoxies, Ect. 20-2521 |
PUR, Unspecified |
Epoxies, Etc.
|
|
Huafon JF-A-5015 |
PUR, Unspecified |
Huafon Group Co., Ltd.
|
|
Baytec® SPR-066A |
PUR-Ether/MDI |
Covestro - PUR
|