Описание материалов:
High density moisture curable polyethylene compound for hot and cold water plumbing pipe. Suitable for SDR 9 pipe applications in continuous service at operating conditions of 140°F and 80 psi.
Pexidan® L/T (including L/T Eclipse) is a high density PEX System consisting of a silane grafted base-compound A-1001 and a catalyst masterbatch CAT-003. When mixed and extruded in the proper proportions, the two-component system results in a material that is crosslinkable by exposure to moisture or by immersion in hot water at 90-95°C. Pexidan® L/T is listed by NSF International to Standards 14 and 61 and to Canadian Standards Association standard B137.5. NSF certification to ASTM F 876 and ASTM F 2023 testifies to its superior resistance to oxidation by hot, chlorinated water. Pexidan® L/T is permitted to be used in domestic continuous re-circulation systems and is listed by NSF as a NSF-pw CL5 / PEX 5006 material.
| Главная Информация | |
|---|
| Характеристики | - Высокая плотность
- Антиоксидант
- Crosslinkable
|
| Используется | |
| Рейтинг агентства | - ASTM F 2023
- ASTM F 876
- CSA B137.5
- Утверждено NSF 14
- Утверждено NSF 61
|
| Формы | |
| Метод обработки | - Экструзионная формовка труб
- Экструзия
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 0.944 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Степень перекрестного соединения | > 70 | % | ASTM D2765 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Основы гидростатического дизайна-
@ 68% DOC | | | ASTM D2837 |
| 23°C | 8.62 | MPa | ASTM D2837 |
| 82°C | 5.52 | MPa | ASTM D2837 |
| 93°C | 4.34 | MPa | ASTM D2837 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Время индукции окисления | > 50 | min | ASTM D3895 |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Горячее удлинение 1 | | | Internal method |
| elongation under load
: 150°C | 30 | % | Internal method |
| permanent elongation (set) after cooling
: 150°C | 0.0 | % | Internal method |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура головы | 365 | °F | |
| Винтовое охлаждение | neutral | | |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | | | ISO 527-2 |
| -40°C | 2310 | MPa | ISO 527-2 |
| 0°C | 1690 | MPa | ISO 527-2 |
| 23°C | 862 | MPa | ISO 527-2 |
| Прочность на растяжение | | | ASTM D638 |
| Yield | 20.0 | MPa | ASTM D638 |
| Fracture | 21.0 | MPa | ASTM D638 |
| Удлинение при растяжении (Break) | 400 | % | ASTM D638 |
| Флекторный модуль | | | ISO 178 |
| -40°C | 517 | MPa | ISO 178 |
| 0°C | 379 | MPa | ISO 178 |
| 23°C | 207 | MPa | ISO 178 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Викат Температура размягчения | 124 | °C | ASTM D1525 |
| CLTE-
Поток (-100 to 85°C) | 1.5E-4 | cm/cm/°C | ASTM D696 |
| Удельный нагрев (23°C) | 1920 | J/kg/°C | |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Curing can be done in the following ways:
by immersion in hot water at 90-95°C
by exposure to low pressure steam
In all cases curing time depends on pipe wall thickness, temperature, relative humidity and any packaging used.Typical values reported above (except MFR) are obtained from samples cured in hot water (6 hours @ 95°C). |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Зона цилиндра 1 темп. | 160 - 177 | °C | |
| Зона цилиндра 2 температура. | 160 - 177 | °C | |
| Зона цилиндра 3 темп. | 160 - 177 | °C | |
| Зона цилиндра 4 темп. | 160 - 177 | °C | |
| Температура матрицы | 185 | °C | |
| Примечание |
|---|
| 1 . | 15 minutes, 0.2 N/mm² load |