Описание материалов:
Baytec SPR-256D is a two-component, 100%-solids spray system with a Shore hardness of 56D. The isocyanate component is a modified diphenylmethane diisocyanate (MDI) prepolymer, and the polyol component is a polyether polyol blend. Baytec SPR-256D spray system is typically used for in-mold spray applications with polyurethane structural composites. As with any product, use of Baytec SPR-256D in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.07 | g/cm³ | ASTM D792 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore D) | 56 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение (Break) | 16.5 | MPa | ASTM D638 |
| Удлинение при растяжении (Break) | 54 | % | ASTM D638 |
| Удлинение-
Влажное старение 1 | 64 | % | |
| Растяжимое напряжение при выходе 2 | 10.3 | MPa | |
| Прочность на растяжение 3 | 15.2 | MPa | |
| Тепловой | Номинальное значение | | Метод испытания |
|---|
| Холодное сопротивление | No Cracking | | SAE J323 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Запотевание | 98 | % | GM 9305P |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Устойчивость к истиранию (1000 Cycles, 1000 g, H-18 Wheel) | 166 | mg | ASTM D3489 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tear Strength | | | |
| -- 4 | 56.6 | kN/m | ASTM D624 |
| Cracking | 13 | kN/m | ASTM D1938 |
| Термокомплект | Номинальное значение | | |
|---|
| Компоненты термокомплекта | | | |
| Component a | Mixing ratio by weight: 110, mixing ratio by capacity: 100 | | |
| Component B | Mixing ratio by weight: 100, mixing ratio by capacity: 100 | | |
| Дополнительная информация |
|---|
| Part A
Type: Isocyanate
Appearance: Clear amber liquid
Specific Gravity @ 25°C: 1.14
Viscosity @25°C: 600 mPa
Flash Point, PMCC: 210°C
NCO: 19 wt%
Part B
Type: Polyol
Appearance: Gray opaque liquid
Specific Gravity @ 25°C: 1.04
Viscosity @25°C: 1500 mPa-s
Flash Point, PMCC: 201°C
Hydroxyl Number: 233 mg KOH/g
Processing Temperature: 19 to 66°CGel Time: 5 to 15 secTack-Free: 30 sec |
| Примечание |
|---|
| 1 . | GM 7001, K9588 |
| 2 . | 5 hours at 120°C, 100% RH, GM 7001, X9588 |
| 3 . | 21 days at 120°C, GM 7001M, W6655 |
| 4 . | C mould |
| Тип материала |
Категория |
Производитель |
|
BJB Polyurethane TC-850 A/B |
PUR, Unspecified |
BJB Enterprises, Inc.
|
|
Foam-It® 10 SLOW |
PUR, Unspecified |
Smooth-On, Inc
|
|
Epoxies, Ect. 20-2390 |
PUR, Unspecified |
Epoxies, Etc.
|
|
Huafon JF-W-3015A |
PUR, Unspecified |
Huafon Group Co., Ltd.
|
|
Baypreg® F 315 (25 mm Glass Mat Reinforced Sandwich) |
PUR, Unspecified |
Covestro - PUR
|
|
Andur 7500 DP/Curene® 442 |
PUR-Ether/TDI |
Anderson Development Company
|