LUVOCOM® 94-8839/ES

Категория	LDPE, Low Density Polyethylene
Производитель	LEHVOSS Group
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	xmwdxR_LUVOCOM948839ES.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®94-8839/ES is a low density polyethylene material containing stainless steel fibers. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 94-8839/ES are:

Conductivity

Electromagnetic shielding (EMI)

Typical application areas include:

engineering/industrial accessories

textile/fiber

Automotive Industry

business/office supplies

Главная Информация
Наполнитель/армирование	Волокно из нержавеющей стали
Характеристики	Проводящий Электромагнитное Экранирование (EMI) Статическая проводимость
Используется	Тонкостенные детали Текстильные изделия Инженерные аксессуары Применение в автомобильной области Бизнес-оборудование
Внешний вид	Натуральный цвет

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.20	g/cm³	ISO 1183
Формовочная усадка	1.0 - 1.6	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.10	%

Твердость	Номинальное значение	Единица измерения	Метод испытания
Твердость дюрометра (Shore D)	48		ISO 868

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	400	MPa	ISO 527-2
Tensile Stress (Break)	10.0	MPa	ISO 527-2
Растяжимое напряжение (Yield)	20	%	ISO 527-2

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Charpy Unnotched Impact Strength
-30°C	No Break		ISO 179/1fU
23°C	80	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Температура непрерывного использования	70.0	°C	UL 746B
Максимальная рабочая температура- Короткий срок	110	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	1.0 - 3.2	ohms	IEC 60167

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Викат Температура размягчения	80.0	°C	ISO 306/A

Электрический	Номинальное значение	Единица измерения	Метод испытания
Удельное сопротивление поверхности	< 3.2	ohms	IEC 60093

Инъекция	Номинальное значение	Единица измерения
Температура сушки- Осушитель сушилка	85	°C
Время сушки- Осушитель сушилка	2.0 - 3.0	hr
Задняя температура	160 - 200	°C
Средняя температура	170 - 220	°C
Передняя температура	180 - 240	°C
Температура сопла	190 - 250	°C
Температура обработки (расплава)	230	°C
Температура формы	30 - 80	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information If originally sealed containers are used, it is normally possible to omit the predrying stage. If PTFE materials are not predried, an increase in deposits inside the mould may occur. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information If originally sealed containers are used, it is normally possible to omit the predrying stage. If PTFE materials are not predried, an increase in deposits inside the mould may occur. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Тип материала	Категория	Производитель
PRIMALENE WPP593B	LDPE	Southern Polymer, Inc.
ALCUDIA® LDPE PE-023	LDPE	REPSOL
CERTENE™ LDF-0218A	LDPE	Muehlstein
ExxonMobil™ LDPE EVA Copolymers LD 364HE	LDPE	ExxonMobil Chemical
INEOS LDPE 22H760	LDPE	INEOS Olefins & Polymers Europe
Lupolen 2421 K	LDPE	LyondellBasell Industries

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

