| Категория | LDPE, Low Density Polyethylene |
| Производитель | SABIC Americas, Inc. |
| Торговая марка | SABIC® LDPE |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
9BvkNu_SABIC-LDPE-HP4023W.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Product Description
HP4023W is Low Density Polyethylene grade suitable for producing general purpose films and contains slip and antiblock additives. It gives excellent processability and optical properties with good mechanical properties.
Typical Applications
HP4023W can be used for high clarity laundry bags, textile wrapping films, produce bags, zip lock bags.
HP4023W is Low Density Polyethylene grade suitable for producing general purpose films and contains slip and antiblock additives. It gives excellent processability and optical properties with good mechanical properties.
Typical Applications
HP4023W can be used for high clarity laundry bags, textile wrapping films, produce bags, zip lock bags.
| Главная Информация | |
|---|---|
| Добавка |
|
| Характеристики |
|
| Используется |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.923 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/21.6 kg) | 4.0 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 30 | µm | |
| Сектантный модуль | ASTM D882 | ||
| 1% secant, MD : 30 µm, blown film | 60.0 | MPa | ASTM D882 |
| 1% secant, TD : 30 µm, blown film | 170 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 30 µm, blown film | 7.00 | MPa | ASTM D882 |
| TD : Yield, 30 µm, blown film | 7.00 | MPa | ASTM D882 |
| MD : Broken, 30 µm, blown film | 18.0 | MPa | ASTM D882 |
| TD : Broken, 30 µm, blown film | 15.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 270 | % | ASTM D882 |
| TD : Broken, 30 µm, blown film | 540 | % | ASTM D882 |
| Ударное падение Dart (30 µm, Blown Film) | 60 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 30 µm, blown film | 150 | g | ASTM D1922 |
| TD : 30 µm, blown film | 120 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Викат Температура размягчения | 91.0 | °C | ASTM D1525 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 30.0 µm, Blown Film) | 75 | ASTM D2457 | |
| Haze (30.0 µm, Blown Film) | 7.0 | % | ASTM D1003 |
| Дополнительная информация | Номинальное значение | ||
|---|---|---|---|
| Blow-up Ratio | 2.00 - 3.00 | ||
| Properties have been measured by producing 30 µ film with 2.5 BUR using 100% HP4023W. |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура расплава | 160 - 175 | °C |
| Тип материала | Категория | Производитель |
|---|---|---|
| TITANLENE® LDF 260JG | LDPE | Lotte Chemical Titan (M) Sdn. Bhd. |
| Westlake LDPE EF412 | LDPE | Westlake Chemical Corporation |
| ExxonMobil™ LDPE LD 317.09 | LDPE | ExxonMobil Chemical |
| INEOS LDPE 19N430 | LDPE | INEOS Olefins & Polymers Europe |
| SABIC® LDPE 2502X0 | LDPE | Saudi Basic Industries Corporation (SABIC) |
| SABIC® LDPE PCG02 | LDPE | Saudi Basic Industries Corporation (SABIC) |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved