DOWLEX™ 2607GC
| Категория | LLDPE, Linear Low Density Polyethylene Resin |
| Производитель | The Dow Chemical Company |
| Торговая марка | DOWLEX™ |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
vUylHB_DOWLEX-2607GC.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
DOWLEX 2607 GC Polyethylene Resin is specifically designed for large/high output cast film lines to make high performance industrial stretch films.
Films made from DOWLEX 2607 GC Polyethylene Resin exhibit an excellent balance of processability, mechanical and stretchability performance properties.
DOWLEX 2607 GC Polyethylene Resin is to be used as a core resin in coextruded cast film structures for films in the thickness range between 10 and 35 microns.
Complies with:
Films made from DOWLEX 2607 GC Polyethylene Resin exhibit an excellent balance of processability, mechanical and stretchability performance properties.
DOWLEX 2607 GC Polyethylene Resin is to be used as a core resin in coextruded cast film structures for films in the thickness range between 10 and 35 microns.
Complies with:
- EU, No10/2011
- U.S. FDA FCN 741
| Главная Информация | |
|---|---|
| Рейтинг агентства |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.918 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 2.3 | g/10 min | ISO 1133 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 23 | µm | |
| Энергия прокола пленки (23 µm) | 160 | J | |
| Сила прокола пленки (23 µm) | 44.0 | N | |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 23 µm | 8.00 | MPa | ASTM D882 |
| TD : Yield, 23 µm | 8.00 | MPa | ASTM D882 |
| MD : Break, 23 µm | 35.0 | MPa | ASTM D882 |
| TD : Break, 23 µm | 29.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Break, 23 µm | 460 | % | ASTM D882 |
| TD : Break, 23 µm | 700 | % | ASTM D882 |
| Ударное падение Dart (23 µm) | 150 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 23 µm | 190 | g | ASTM D1922 |
| TD : 23 µm | 420 | g | ASTM D1922 |
| Растяжимые свойства пленки-максимальная сила растяжения (23.0 µm) | 37000 | g | Internal method |
| Свойства растяжения пленки-максимальное удлинение (23.0 µm) | 350 | % | Internal method |
| Дополнительная информация |
|---|
| Film Properties: Cast Film fabrication at 250 m/min. |
| Инструкции по экструзии |
|---|
| Fabrication Conditions For Cast Film Extrusion: Chill Roll Temperature: 20 - 40°C Melt Temperature: 220 - 280°C Recommended Gauge Range: 10 - 35 µm |
| Тип материала | Категория | Производитель |
|---|---|---|
| Sinpolene MBB0031 | LLDPE | Teknor Apex Asia Pacific PTE. LTD. |
| Trademark PE LLB1918F | LLDPE | Trademark Plastics Corporation |
| ADMER™ NF642E | LLDPE | Mitsui Chemicals Europe GmbH |
| Hanwha Total PE 4220U | LLDPE | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Petrothene® GA501152 | LLDPE | LyondellBasell Industries |
| MTEGRITY™ LLDPE LL107AH | LLDPE | M. Holland Company |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved