Описание материалов:
Clearflex H&T CLH 108 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants, suitable for cast film extrusion.
Stretch films obtained from Clearflex H&T CLH 108 show excellent optical properties, high fracture mechanical characteristics, together with excellent performances in automatic wrapping machines (holding force, prestretch).
Main Application
Clearflex H&T CLH 108 is suggested for production of very-high pre-stretch film. The combination of high mechanical properties and low gel content can allow "downgauging" for many applications. In addition to that, for its high resistance to tear propagation and to puncture, together with an outstanding holding force, Clearflex H&T CLH 108 is recommended for "critical" packaging (i.e irregular shape loads, presence of sharp edges, etc…) or loads subjected to severe mechanical stresses during transportation.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Антиоксидант
- Сополимер
- Приемлемый пищевой контакт
- Хорошая растяжимость
- Хорошая прочность на разрыв
- Низкая плотность
- Низкий гель
- Октеновый комномер
- Оптика
- Стойкий к проколу
|
| Используется | - Литая пленка
- Упаковка
- Эластичная пленка
|
| Рейтинг агентства | - ЕС пищевой контакт, неуказанный рейтинг
|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.919 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ISO 1133 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Коэффициент трения (vs. Itself - Dynamic, Cast Film) | > 0.50 | | ISO 8295 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 23 | µm | |
| Толщина пленки-рекомендовано/доступно | 8 to 50µm | | |
| Модуль растяжения | | | ISO 527-3 |
| 1% Secant, MD
: 23 µm, Cast Film | 140 | MPa | |
| 1% Secant, TD
: 23 µm, Cast Film | 150 | MPa | |
| Tensile Stress | | | ISO 527-3 |
| MD
: Yield, 23 µm, Cast Film | 9.00 | MPa | |
| TD
: Yield, 23 µm, Cast Film | 10.0 | MPa | |
| MD
: Break, 23 µm, Cast Film | 48.0 | MPa | |
| TD
: Break, 23 µm, Cast Film | 40.0 | MPa | |
| Удлинение при растяжении | | | ISO 527-3 |
| MD
: Break, 23 µm, Cast Film | 600 | % | |
| TD
: Break, 23 µm, Cast Film | 800 | % | |
| Ударное падение Dart 1(23 µm, Cast Film) | 170 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | | | ISO 6383-2 |
| MD
: 23.0 µm | 130.0 | kN/m | |
| TD
: 23.0 µm | 170.0 | kN/m | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура ломкости | < -70.0 | °C | ASTM D746 |
| Викат Температура размягчения | 95.0 | °C | ISO 306/A |
| Температура плавления | 120 | °C | Internal Method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск (45°, 23.0 µm, Cast Film) | 93 | | ASTM D2457 |
| Haze (23.0 µm, Cast Film) | 0.80 | % | ISO 14782 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 220 to 270 | °C | |
| Примечание |
|---|
| 1 . | F50 |
| 2 . | Cast Film |