Описание материалов:
Baydur 728 IBS is a high-density polyurethane structural foam system used in the reaction injection molding (RIM) process. This system incorporates a specially engineered interactive blowing system (IBS) and internal mold release (IMR). The system is supplied as two reactive liquid components. Component A is a polymeric diphenylmethane diisocyanate (PMDI) and Component B is a formulated polyol system containing no CFC- or HCFC-blowing additives.
Baydur 728 IBS system is used in applications requiring a UL94 flammability rating of V-0 and/or 5VA for use in electronic, equipment housing, and appliance markets. The applications typically take advantage of the material's strength, excellent surface finish, and large-part capability. As with any product, use of the Baydur 728 IBS system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Хорошая прочность
- Хорошая поверхность
|
| Используется | - Приборы
- Электрическое/электронное применение
- Корпуса
|
| Метод обработки | - Литье под давлением реакции (обод)
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Формовочная усадка-
Поток (6.35 mm) | 0.70 to 0.95 | % | ASTM D955 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение | | | ASTM D638 |
| Break, 3.18 mm | 22.8 | MPa | |
| Break, 3.96 mm | 35.2 | MPa | |
| Break, 6.35 mm | 30.4 | MPa | |
| Удлинение при растяжении | | | ASTM D638 |
| Break, 3.18 mm | 6.0 | % | |
| Break, 3.96 mm | 10 | % | |
| Break, 6.35 mm | 9.0 | % | |
| Флекторный модуль | | | ASTM D790 |
| 3.18 mm | 1540 | MPa | |
| 3.96 mm | 1760 | MPa | |
| 6.35 mm | 1650 | MPa | |
| Flexural Strength | | | ASTM D790 |
| 3.18 mm | 55.8 | MPa | |
| 3.96 mm | 68.2 | MPa | |
| 6.35 mm | 58.6 | MPa | |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Charpy Unnotched Impact Strength | | | |
| -- 1 | 19 | kJ/m² | Internal Method |
| -- 2 | 25 | kJ/m² | Internal Method |
| Зубчатый изод Impact | | | ASTM D256 |
| 3.18 mm | 21 | J/m | |
| 3.96 mm | 27 | J/m | |
| 6.35 mm | 27 | J/m | |
| Незубчатый изод Impact | | | ASTM D256 |
| 3.18 mm | 160 | J/m | |
| 3.96 mm | 210 | J/m | |
| 6.35 mm | 160 | J/m | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | ASTM D648 |
| 0.45 MPa, Unannealed, 3.18 mm | 70.0 | °C | |
| 0.45 MPa, Unannealed, 3.96 mm | 80.0 | °C | |
| 0.45 MPa, Unannealed, 6.35 mm | 100 | °C | |
| CLTE-
Поток | | | ASTM D696 |
| 70°C, 3.18 mm | 1.1E-4 | cm/cm/°C | |
| 70°C, 3.96 mm | 1.0E-4 | cm/cm/°C | |
| 70°C, 6.35 mm | 9.0E-5 | cm/cm/°C | |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость | | | UL 94 |
| 3.18 mm | V-0
5VA | | |
| 3.96 mm | V-0
5VA | | |
| 6.35 mm | V-0
5VA | | |
| Примечание |
|---|
| 1 . | 0.25 in |
| 2 . | 0.156 in |