Описание материалов:
Baytec MS-051 is a modified diphenylmethane diisocyanate (MDI)-terminated polyester prepolymer used in the manufacture of high-property solid cast polyurethane elastomers. The excellent resilience and low compression-set properties have enabled this material to be used for low-durometer wheels, printing rolls, and squeegee blades. As with any product, use of Baytec MS-051 prepolymer in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Характеристики | - Низкая деформация сжатия
- Гибкий
|
| Используется | |
| Формы | |
| Твердость | Номинальное значение | | Метод испытания |
|---|
| Твердость дюрометра (Shore A) | 93 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Устойчивость к истиранию (1000 Cycles, 1000 g, H-18 Wheel) | 34.0 | mg | ASTM D4066 |
| Отклонение сжатия | | | ASTM D575 |
| 10% | 2.90 | MPa | ASTM D575 |
| 15% | 3.96 | MPa | ASTM D575 |
| 2% | 0.621 | MPa | ASTM D575 |
| 20% | 5.03 | MPa | ASTM D575 |
| 25% | 6.21 | MPa | ASTM D575 |
| 5% | 1.69 | MPa | ASTM D575 |
| 50% | 18.4 | MPa | ASTM D575 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 100% strain | 8.07 | MPa | ASTM D412 |
| 200% strain | 9.89 | MPa | ASTM D412 |
| 300% strain | 11.8 | MPa | ASTM D412 |
| Прочность на растяжение (Break) | 26.3 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 650 | % | ASTM D412 |
| Tear Strength | | | |
| -- 1 | 108 | kN/m | ASTM D624 |
| Cracking | 49 | kN/m | ASTM D1938 |
| Комплект сжатия (70°C, 22 hr) | 19 | % | ASTM D395 |
| Сопротивляемость Bayshore | 54 | % | ASTM D2632 |
| Дополнительная информация |
|---|
| Appearance: Light amber liquidNCO: 4.9 to 5.2 wt%Flash Point, PMCC: >93°CSpecific Gravity at 80°C: 1.18Specific Gravity at 100°C: 1.17Viscosity at 80°C: 2700 mPa-sViscosity at 700°C: 115 mPa-sNCO/OH Ratio: 1.10Stoichiometry: 90% TheoryPrepolymer Temperature: 100 to 110°CExtender Temperature: 100 to 110°CMold Temperature: 100 to 110°CPot Life: 10 to 15 minDemold: 60 min |
| Тип материала |
Категория |
Производитель |
|
Xuchuan XCG-100 |
PUR, Unspecified |
Xuchuan Chemical (Suzhou) Co., Ltd
|
|
Xuchuan XCD-675A |
PUR, Unspecified |
Xuchuan Chemical (Suzhou) Co., Ltd
|
|
Baydur® 684 (15 pcf) |
PUR, Unspecified |
Covestro - PUR
|
|
Epoxies, Ect. 20-2330 |
PUR, Unspecified |
Epoxies, Etc.
|
|
Huafon JF-S-8080 |
PUR, Unspecified |
Huafon Group Co., Ltd.
|
|
Huafon JF-S-M8085 |
PUR, Unspecified |
Huafon Group Co., Ltd.
|