Braskem PE EF2222
| Категория | LDPE, Low Density Polyethylene |
| Производитель | Braskem |
| Торговая марка | Braskem PE |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
tpB1I2_Braskem-PE-EF2222.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
EF2222 is a low-density polyethylene (LDPE), with excellent processability and low gel content. Those features allow production of thin and highly uniform films.
Additives:
No additives
Application:
Smooth or embossed films for diapers, disposable sheets, etc. Films for lamination. Injection-Blow Molding. Foamed applications.
Process:
Recommended processing conditions for film extrusion about 145 - 190 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee.
Additives:
No additives
Application:
Smooth or embossed films for diapers, disposable sheets, etc. Films for lamination. Injection-Blow Molding. Foamed applications.
Process:
Recommended processing conditions for film extrusion about 145 - 190 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee.
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.922 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 2.2 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Сектантный модуль | ASTM D882 | ||
| 1% secant, MD : 38 µm | 170 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm | 210 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Fracture, 38 µm | 30.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 20.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Fracture, 38 µm | 420 | % | ASTM D882 |
| TD : Fracture, 38 µm | 1100 | % | ASTM D882 |
| Ударное падение Dart 1(38 µm) | 70 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 480 | g | ASTM D1922 |
| TD : 38 µm | 150 | g | ASTM D1922 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (60°, 38.0 µm) | 100 | ASTM D2457 | |
| Haze | 6.0 | % | ASTM D1003 |
| Инструкции по экструзии |
|---|
| Recommended Blow Film Extrusion Conditions: Temperature Profile: 145°C to 190°C Mass Temperature: 190°C Blow up Ratio: 2.0 to 3.0 : 1 Die Gap: 1.0 mm |
| Примечание | |
|---|---|
| 1 . | F50 |
| Тип материала | Категория | Производитель |
|---|---|---|
| Westlake LDPE EC1390AA | LDPE | Westlake Chemical Corporation |
| AEI SX522A:CM401 and SX522A:CM401CDS | LDPE | AEI Compounds Limited |
| Braskem PE SPB681/59 | LDPE | Braskem America Inc. |
| Hypel® PELD50/.924 | LDPE | Entec Polymers |
| Polybilt™ Bitumen Modifier 101 | LDPE | ExxonMobil Chemical |
| LUVOCOM® 94-8839 | LDPE | Lehmann & Voss & Co. |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved