MonoSol® AF A200
| Категория | PVOH, Polyvinyl Alcohol |
| Производитель | MonoSol, LLC |
| Торговая марка | MonoSol® |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
tf8VUs_MonoSol-AF-A200.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
MonoSol AF A200 is a PVOH based thermoplastic film, soluble in hot water and manufactured using MonoSol AF's proprietary blown film technology.
MonoSol AF A200 is a typical grade of PVOH hot water-soluble film. It is soluble above 60°C with agitation. It has limited cold wet strength and is primarily used for hospital laundry bags where the bulk of the linen is dry. It can also be used on some VFFS packaging machinery for chemical portion packaging applications where the pack is being put into an environment with water above 60°C with agitation. Available thickness range is 20 micron (0.8 mil) to 80 micron (3.1 mil).
MonoSol AF A200 is a typical grade of PVOH hot water-soluble film. It is soluble above 60°C with agitation. It has limited cold wet strength and is primarily used for hospital laundry bags where the bulk of the linen is dry. It can also be used on some VFFS packaging machinery for chemical portion packaging applications where the pack is being put into an environment with water above 60°C with agitation. Available thickness range is 20 micron (0.8 mil) to 80 micron (3.1 mil).
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Содержание влаги (23 °C) 1 | 6.7 | wt% | |
| Растворимость 2 | |||
| Disintegration : 60°C, 20.0 µm | 1.0 | sec | |
| Disintegration : 70°C, 20.0 µm | 1.0 | sec | |
| Dissolution : 60°C, 20.0 µm | 430.0 | sec | |
| Dissolution : 70°C, 20.0 µm | 300.0 | sec |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Выход (20,0 мкм) | 40.1 | m²/kg | ASTM D4321 |
| Толщина пленки протестирована | 20 | µm | |
| Толщина пленки-рекомендовано/доступно | 20 µm to 80 µm | ||
| Сектантный модуль | ASTM D882, ISO 527-3 | ||
| 10%, MD : 20 µm | 238 | MPa | |
| 100%, MD : 20 µm | 64.8 | MPa | |
| 10%, TD : 20 µm | 290 | MPa | |
| 100%, TD : 20 µm | 45.5 | MPa | |
| Прочность на растяжение | |||
| MD : Break, 20 µm | 71.7 | MPa | ASTM D882 |
| TD : Break, 20 µm | 77.9 | MPa | ASTM D882 |
| MD : 20 µm | 71.7 | MPa | ISO 527-3 |
| TD : 20 µm | 77.9 | MPa | ISO 527-3 |
| Удлинение при растяжении | ASTM D882, ISO 527-3 | ||
| MD : Break, 20 µm | 130 | % | |
| TD : Break, 20 µm | 230 | % | |
| Ударное падение Dart (20 µm) | 290 | g | ASTM D1709, DIN 53433 |
| Elmendorf Tear Strength | |||
| MD : 20 µm | 300 | g | ASTM D1922 |
| TD : 20 µm | 300 | g | ASTM D1922 |
| MD : 20 µm | 0.031 | N | ISO 6383-2 |
| TD : 20 µm | 0.031 | N | ISO 6383-2 |
| Примечание | |
|---|---|
| 1 . | 50%RH |
| 2 . | Distilled Water (MSTM 205) |
| Тип материала | Категория | Производитель |
|---|---|---|
| Mowiflex™ TC 232 | PVOH | Kuraray Co., Ltd. |
| DENKA POVAL PC-5500 | PVOH | Denka Company Limited |
| Mowiol® 4-88 G2 | PVOH | Kuraray Co., Ltd. |
| Kuraray Poval® PVA 117 | PVOH | Kuraray Co., Ltd. |
| Mowiol® 40-88 | PVOH | Kuraray Co., Ltd. |
| MonoSol® M3030 | PVOH | MonoSol, LLC |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved