Описание материалов:
Bayflex XGT-16 Black is a black-pigmented elastomeric polyurethane system used in the reaction injection molding (RIM) process. The formulated system is supplied as two liquid components: Component A is a diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol system. Note: The polyol component phase-separates upon standing and must be thoroughly mixed via mechanical means prior to use.
Bayflex XGT-16 Black system has a flexural modulus of 16,000 psi* at room temperature. It is used in applications requiring excellent impact properties, such as bumpers for buses and other vehicles. As with any product, use of the Bayflex XGT-16 Black system in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Характеристики | |
| Используется | - Забор для автомобильных дорожных ограждений
|
| Внешний вид | |
| Формы | |
| Метод обработки | - Литье под давлением реакции (обод)
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.04 | g/cm³ | ASTM D792, ASTM D1622 |
| Формовочная усадка-
Поток (3.18 mm) | 0.80 - 0.90 | % | Internal method |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра | | | ASTM D2240 |
| Shaw A, 3.18mm | 94 | | ASTM D2240 |
| Shaw D, 3.18mm | 45 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Флекторный модуль (3.18 mm) | 110 | MPa | ASTM D790 |
| Устойчивость к истиранию (1000 Cycles, 1.0E 6g, H-18 wheel) | 200 | mg | ASTM D1044 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение (Break, 3.18 mm) | 16.5 | MPa | ASTM D412 |
| Удлинение при растяжении (Break, 3.18 mm) | 250 | % | ASTM D412 |
| Tear Strength 1(3.18 mm) | 78.8 | kN/m | ASTM D624 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| CLTE-
Поток (3.18 mm) | 1.4E-4 | cm/cm/°C | ASTM D696 |
| Термокомплект | Номинальное значение | Единица измерения | |
|---|
| Компоненты термокомплекта 2 | | | |
| Component a | Mixing ratio by weight: 80, mixing ratio by capacity: 68 | | |
| Component B | Mixing ratio by weight: 100, mixing ratio by capacity: 100 | | |
| Срок годности (30°C) | 26 | wk | |
| Дополнительная информация |
|---|
| Part A
Type: Isocyanate
Appearance: Water white to clear pale yellow liquid
Specific Gravity @ 25°C: 1.21
Viscosity @25°C: 700 mPa-s
Flash Point PMCC: 213 °C
Part B
Type: Polyol
Appearance: Black liquid
Specific Gravity @ 25°C: 1.04
Viscosity @25°C: 600 mPa-s
Flash Point PMCC: 112 °C
Water: 0.09 wt%
Hydroxyl Number: 229 mg KOH/g
Molding Parameters
Material Temperature: 32 to 38 °C
Mold Temperature: 60 to 70 °C
Typical Cure Time, 0.125 in: 120 to 180 sec
Polyol Nucleation - Specific Gravity: 0.75 to 0.80 0
shot time: 5 to 6 sec |
| Примечание |
|---|
| 1 . | C mould |
| 2 . | 1.05 Index |