Arak LLDPE LL0220AA
| Категория | LLDPE, Linear Low Density Polyethylene |
| Производитель | Shazand (Arak) Petrochemical Corporation |
| Торговая марка | Arak LLDPE |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
sspYsV_Arak-LLDPE-LL0220AA.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
LL0220AA is a linear low density polyethylene copolymer containing butene-1 as a co-monomer.
LL0220AA has been specially developed for production of hand wrap and other cast stretch films such as oriented tapes. It can also be used as a blending partner in LDPE or LLDPE in both cast and blown film applications.
LL0220AA offers the following advantages when it processed by the cast extrusion process:
LL0220AA also can be used as compounds for low voltage power cable insulation or fibre optic jacketing.
LL0220AA should be processed in machinery designed for LLDPE.
Melt temperature range in the cast process are normally 240°C-280°C and in lean blends for blown film are 165°C-215°C.
LL0220AA should be stored in the dry condition below the 50°C and avoided from the exposure of direct sunlight.
* LL0220AA is suitable for food contact.
LL0220AA has been specially developed for production of hand wrap and other cast stretch films such as oriented tapes. It can also be used as a blending partner in LDPE or LLDPE in both cast and blown film applications.
LL0220AA offers the following advantages when it processed by the cast extrusion process:
- Good balance of mechanical properties.
- Good optical properties.
- Good cling performance.
LL0220AA also can be used as compounds for low voltage power cable insulation or fibre optic jacketing.
LL0220AA should be processed in machinery designed for LLDPE.
Melt temperature range in the cast process are normally 240°C-280°C and in lean blends for blown film are 165°C-215°C.
LL0220AA should be stored in the dry condition below the 50°C and avoided from the exposure of direct sunlight.
* LL0220AA is suitable for food contact.
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.917 to 0.920 | g/cm³ | ASTM D2838 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 2.0 to 2.5 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 38 | µm | |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield | 10.0 | MPa | |
| TD : Yield | 9.00 | MPa | |
| MD : Break | 40.0 | MPa | |
| TD : Break | 31.0 | MPa | |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Break | 600 | % | |
| TD : Break | 810 | % | |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 90 | g | |
| TD : 25 µm | 280 | g |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°) | 50 | ASTM D2457 | |
| Haze | 13 | % | ASTM D1003 |
| Дополнительная информация | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Blown Film Melt Temperature | 165 to 215 | °C | |
| Температура плавления литой пленки | 240 to 280 |
| Тип материала | Категория | Производитель |
|---|---|---|
| Sinpolene MBW0351 | LLDPE | Teknor Apex Asia Pacific PTE. LTD. |
| VENELENE® 2706 | LLDPE | Poliolefinas Internacionales, C.A. (Polinter) |
| VENELENE® 11S1 | LLDPE | Poliolefinas Internacionales, C.A. (Polinter) |
| DOWLEX™ 2045G | LLDPE | The Dow Chemical Company |
| Indothene LL 20FS020 | LLDPE | Reliance Industries Limited |
| Osterlene® LLSH0917SAH | LLDPE | Osterman & Company |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved