Описание материалов:
WESTLAKE Hifor Clear Polyethylene SC74580 polymer is a high strength and high clarity linear low density polyethylene designed for blown film extrusion that contains no slip and no antiblock. It does contain processing aid. Blown films produced with this resin exhibit good toughness, with exceptional gloss and clarity for a product of this density, yet film blocking in substantially lower than one might expect. Film stiffness is also higher than one might expect for this density. It works well in many shrink film applications. Contact Westlake for further information on the regulatory staturs.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Хорошая прочность на разрыв
- Хорошая прочность
- Глянцевый
- Средняя четкость
|
| Используется | - Пленка
- Пищевая упаковка
- Упаковка
|
| Рейтинг агентства | - Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 177,1520
|
| Внешний вид | |
| Формы | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.926 | g/cm³ | ASTM D4883 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.60 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Сектантный модуль | | | ASTM D882 |
| 1% Secant, MD | 324 | MPa | |
| 1% Secant, TD | 379 | MPa | |
| Прочность на растяжение | | | ASTM D882 |
| MD
: Break | 58.0 | MPa | |
| TD
: Break | 38.0 | MPa | |
| Удлинение при растяжении | | | ASTM D882 |
| MD
: Break | 600 | % | |
| TD
: Break | 950 | % | |
| Ударное падение Dart | 100 | g | ASTM D1709 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск (45°) | 82 | | ASTM D2457 |
| Haze | 4.0 | % | ASTM D1003 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура обработки (расплава) | 204 to 216 | °C | |