Описание материалов:
ELITE* 5500G Enhanced Polyethylene Resin is a copolymer produced via INSITE* Technology. It offers an exceptional combination of processability, low heat seal initiation temperature, package integrity, optical properties, and tear strength.
Complies with:
- A high performance sealant for food and specialty packaging films
- Outstanding combination of seal performance, caulkability, optics, and tear strength
- Easy processability on blown and cast film extrusion equipment
Complies with:
- U.S. FDA FCN 424
- EU, No 10/2011
- Canadian HPFB No Objection
- Consult the regulations for complete details.
| Главная Информация | |
|---|---|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.914 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 25 | µm | |
| Энергия прокола пленки | 5.65 | J | Internal method |
| Сила прокола пленки | 62.3 | N | Internal method |
| Сопротивление проколу пленки | 29.0 | J/cm³ | Internal method |
| Прочность пленки | ASTM D882 | ||
| MD | 82.7 | J/cm³ | ASTM D882 |
| TD | 91.0 | J/cm³ | ASTM D882 |
| Сектантный модуль | ASTM D882 | ||
| 1% secant, MD | 162 | MPa | ASTM D882 |
| 2% secant, MD | 141 | MPa | ASTM D882 |
| 1% secant, TD | 193 | MPa | ASTM D882 |
| 2% secant, TD | 165 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield | 18.3 | MPa | ASTM D882 |
| TD : Yield | 10.3 | MPa | ASTM D882 |
| MD : Fracture | 41.4 | MPa | ASTM D882 |
| TD : Fracture | 37.9 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Fracture | 400 | % | ASTM D882 |
| TD : Fracture | 500 | % | ASTM D882 |
| Ударное падение Dart | 650 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 350 | g | ASTM D1922 |
| TD | 600 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Викат Температура размягчения | 97.0 | °C | ASTM D1525 |
| Температура плавления (DSC) | 122 | °C | Internal method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°) | 45 | ASTM D2457 | |
| Haze | 12 | % | ASTM D1003 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура расплава | 226 | °C |
| Инструкции по экструзии |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；24:1 L/D 螺杆类型：DSB II 模具间隙：70 密尔 (1.8 mm) 熔体温度：425°F 输出：模具周长的 12 磅/小时/英寸 模具直径：8 英寸 放大比：2.5:1 螺杆速度：42 rpm 冷冻线高度：47 英寸 |
| Тип материала | Категория | Производитель |
|---|---|---|
| Generic EPE | EPE | Generic |
| ELITE™ AT 6401 | EPE | The Dow Chemical Company |
| ELITE™ 5101G | EPE | The Dow Chemical Company |
| ELITE™ 5400GS | EPE | The Dow Chemical Company |
| ELITE™ AT 6111 | EPE | The Dow Chemical Company |
| ELITE™ CS 6085B | EPE | The Dow Chemical Company |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved