Описание материалов:
Menzolit® SMC 2400 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens.
Menzolit® SMC 2400 is a SMC with extraordinary fire retardancy. The glass level has been selected to combine mouldability with strength and stiffness properties. The fire retardancy is especially high, and the material is virtually nonburnable. In case of fire smoke is released to a small extent. Smoke is, except for carbon monoxyde non-toxic! This makes SMC 2400 very suitable for railway interior or exterior applications, like wall panels, window frames, lugage bins, seat shells and structures or similar rail way components. Fire safe furniture or sanitary furniture on ships, trains or prison cells are another typical use. Within the electrical industry it is used for arc quenching chambers or switch gear components that are exposed to high power switching operations and resulting electrical arcs (peak loads of temperature and fire).
| Главная Информация | |
|---|
| Наполнитель/армирование | - Стекло \ Mineral, 25% наполнитель по весу
|
| Характеристики | - Огнестойкий
- Хорошая плавность
- Хорошая жесткость
- Хорошая прочность
- Без галогенов
- Высокая термостойкость
- Низкий уровень дыма
|
| Используется | - Электрическое/электронное применение
- Мебель
|
| Внешний вид | |
| Формы | - Smc-лист формовочный состав
|
| Метод обработки | |
| Код маркировки деталей (ISO 11469) | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 1.90 | g/cm³ | ISO 1183 |
| Формовочная усадка | | | |
| -- 1 | 0.0 | % | DIN 53464 |
| -- | 0.080 | % | ISO 2577 |
| Поглощение воды (Saturation, 23°C) | < 0.50 | % | ISO 62 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения (Compression Molded) | 9000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 58.0 | MPa | ISO 527-2 |
| Флекторный модуль (Compression Molded) | 9000 | MPa | ISO 178 |
| Флекторный стресс (Compression Molded) | 140 | MPa | ISO 178 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность (Compression Molded) | 70 | kJ/m² | ISO 179 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | °C | ISO 75-2/A |
| Температура непрерывного использования | 165 | °C | Internal Method |
| Температура перехода стекла | 170 | °C | DSC |
| CLTE-
Поток | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельное сопротивление поверхности | 1.0E+12 | ohms | IEC 60093 |
| Сопротивление громкости | 1.0E+15 | ohms·cm | IEC 60093 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость (3.00 mm) | V-0 | | UL 94 |
| Температура зажигания провода свечения | 960 | °C | IEC 60695-2-13 |
| Индекс кислорода | 70 | % | ISO 4589-2 |
| Дополнительная информация | Номинальное значение | | Метод испытания |
|---|
| Glow Bar | Level BH 2 <= 10 | | IEC 60707-3 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 135 to 150 | °C | |
| Давление впрыска | 8.00 to 10.0 | MPa | |
| Примечание |
|---|
| 1 . | Post Molding Shrinkage |