TOTAL Polyethylene HDPE 6420
| Категория | HDPE, High Density (MMW) Polyethylene , HDPE, MMW |
| Производитель | TOTAL Refining & Chemicals |
| Торговая марка | TOTAL Polyethylene |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
ryLQZQ_TOTAL-Polyethylene-HDPE-6420.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
TOTAL Polyethylene 6420 is a high density (MMW) polyethylene material,. This product is available in North America or Asia Pacific region. The processing method is: film extrusion.
The main features of TOTAL Polyethylene 6420 are:
Typical application areas include:
The main features of TOTAL Polyethylene 6420 are:
- Comply with REACH standard
- odorless/tasteless channel
- High stiffness
- Good processability
Typical application areas include:
- bag/lining
- Movie
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.962 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 2.0 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 55 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Сектантный модуль 1 | ASTM D882A | ||
| 1% secant, MD : 25 µm, blown film | 862 | MPa | ASTM D882A |
| 2% secant, MD : 25 µm, blown film | 689 | MPa | ASTM D882A |
| 1% secant, TD : 25 µm, blown film | 883 | MPa | ASTM D882A |
| 2% secant, TD : 25 µm, blown film | 703 | MPa | ASTM D882A |
| Прочность на растяжение 2 | ASTM D882A | ||
| MD : Yield, 25 µm, blown film | 26.2 | MPa | ASTM D882A |
| TD : Yield, 25 µm, blown film | 27.6 | MPa | ASTM D882A |
| MD : Broken, 25 µm, blown film | 51.7 | MPa | ASTM D882A |
| TD : Broken, 25 µm, blown film | 23.4 | MPa | ASTM D882A |
| Удлинение при растяжении 3 | ASTM D882A | ||
| MD : Broken, 25 µm, blown film | 700 | % | ASTM D882A |
| TD : Broken, 25 µm, blown film | 700 | % | ASTM D882A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 24 | g | ASTM D1922 |
| MD : 51 µm, Coextruded Film 4 | 70 | g | ASTM D1922 |
| TD : 25 µm, blown film | 390 | g | ASTM D1922 |
| TD : 51 µm, Coextruded Film 5 | 500 | g | ASTM D1922 |
| Скорость передачи водяного пара | ASTM F1249 | ||
| 38°C, 25 µm, blown film | 3.9 | g/m²/24 hr | ASTM F1249 |
| 38°C, 51 µm, Coextruded Film 6 | 2.9 | g/m²/24 hr | ASTM F1249 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура расплава | 199 - 210 | °C |
| Инструкции по экструзии |
|---|
| Recommended BUR: 2.0 to 3.5Recommended FLH/D: 4.0 to 6.0 |
| Примечание | |
|---|---|
| 1 . | 25 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | A/B/B 25/50/25% layer distribution LDPE/6420/6420, 2.5 BUR |
| 5 . | A/B/B 25/50/25% layer distribution LDPE/6420/6420, 2.5 BUR |
| 6 . | A/B/B 25/50/25% layer distribution LDPE/6420/6420, 2.5 BUR |
| Тип материала | Категория | Производитель |
|---|---|---|
| DOW™ HDPE DMDA-8907 HEALTH+™ | HDPE | The Dow Chemical Company |
| Alathon® M6080UV | HDPE | LyondellBasell Industries |
| Braskem PE HD 7255 LS-L | HDPE | Braskem |
| Kazan HDPE 273-285 | HDPE | Kazanorgsintez Joint Stock Company |
| PETILEN YY S 0452 | HDPE | PETKIM Petrokimya Holding A.S. |
| ExxonMobil™ HDPE HYA 600 | HDPE, UHMW | ExxonMobil Chemical |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved