Ultramid® 8267G HS BK-102
Описание материалов:
Ultramid 8267G HS BK-102 is a heat stabilized, black pigmented, 40% mineral and glass fiber reinforced PA6 injection molding compound. It possesses a balance of engineering properties in combination with excellent dimensional stability, low warp and resistance to sink-mark formation. It exhibits high strength, rigidity, and good heat distortion temperature. It resists creep under load and the heat stabilizer system extends its retention of properties at elevated temperatures. It has good chemical resistance to greases, oils and hydrocarbons.
Applications
Ultramid 8267G HS BK-102 is generally recommended for applications such as rotors, wheels, rims, timing belt covers, automotive cooling fans and shrouds.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Стекло \ Mineral, 40% наполнитель по весу
|
| Добавка | |
| Характеристики | - Хорошая химическая стойкость
- Хорошее сопротивление ползучести
- Хорошая стабильность размеров
- Хороший поток
- Устойчивость к смазке
- Стабилизация тепла
- Высокая жесткость
- Высокая прочность
- Устойчивость к углеводородам
- Низкий уровень защиты
- Маслостойкий
|
| Используется | - Автомобильные Приложения
- Колеса
|
| Рейтинг агентства | |
| Соответствие RoHS | |
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Многоточечные данные | - Изоляционный стресс против деформации (ISO 11403-1)
- Сектантный модуль против деформации (ISO 11403-1)
- Модуль сдвига против температуры (ISO 11403-1)
- Вязкость по сравнению со скоростью сдвига (ISO 11403-2)
|
| Физический | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.48 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Формовочная усадка-
Поток (3.18 mm) | 0.40 | -- | % | |
| Поглощение воды | | | | |
| 24 hr | 0.90 | -- | % | ASTM D570 |
| 23°C, 24 hr | 0.90 | -- | % | ISO 62 |
| Saturation | 5.7 | -- | % | ASTM D570 |
| Saturation, 23°C | 5.7 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 1.6 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.6 | -- | % | ISO 62 |
| Твердость | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale) | 121 | -- | | ASTM D785 |
| Твердость мяча | 220 | -- | MPa | ISO 2039-1 |
| Механические | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | | | | ISO 527-2 |
| -40°C | 9790 | -- | MPa | |
| 23°C | 8300 | 4160 | MPa | |
| 80°C | 3530 | -- | MPa | |
| 121°C | 2740 | -- | MPa | |
| Прочность на растяжение | | | | |
| Break, 23°C | 130 | 67.0 | MPa | ASTM D638 |
| Break, 23°C | 125 | 67.0 | MPa | ISO 527-2 |
| Удлинение при растяжении (Break, 23°C) | 3.0 | 14 | % | ASTM D638, ISO 527-2 |
| Флекторный модуль | | | | |
| 23°C | 7930 | -- | MPa | ASTM D790 |
| 23°C | 7200 | 3680 | MPa | ISO 178 |
| Flexural Strength | | | | |
| 23°C | 215 | -- | MPa | ASTM D790 |
| 23°C | 195 | 90.0 | MPa | ISO 178 |
| Воздействие | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Ударная прочность | | | | ISO 179 |
| -30°C | 3.5 | -- | kJ/m² | |
| 23°C | 5.0 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 52 | -- | kJ/m² | ISO 179 |
| Зубчатый изод Impact | | | | |
| 23°C | 55 | -- | J/m | ASTM D256 |
| -40°C | 4.0 | -- | kJ/m² | ISO 180 |
| 23°C | 6.0 | -- | kJ/m² | ISO 180 |
| Drop Impact Resistance (23°C) | 2.03 | -- | J | Internal Method |
| Тепловой | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature | | | | |
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 202 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 200 | -- | °C | ISO 75-2/A |
| Пиковая температура плавления | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE | | | | |
| Flow | 3.1E-5 | -- | cm/cm/°C | ASTM E831 |
| Flow | 3.0E-5 | -- | cm/cm/°C | |
| Transverse | 6.7E-5 | -- | cm/cm/°C | |
| RTI Elec (1.50 mm) | 105 | -- | °C | UL 746 |
| RTI Imp (1.50 mm) | 105 | -- | °C | UL 746 |
| RTI Str (1.50 mm) | 105 | -- | °C | UL 746 |
| Электрический | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Сопротивление громкости | | | | |
| 1.50 mm | > 1.0E+13 | -- | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Воспламеняемость | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Огнестойкость (1.50 mm) | HB | -- | | UL 94 |
| Инъекция | Сухой | Единица измерения | |
|---|
| Температура сушки | 83.0 | °C | |
| Время сушки | 2.0 to 4.0 | hr | |
| Рекомендуемая максимальная влажность | 0.15 | % | |
| Температура обработки (расплава) | 270 to 295 | °C | |
| Температура формы | 80.0 to 95.0 | °C | |
| Давление впрыска | 3.50 to 12.5 | MPa | |
| Скорость впрыска | Fast | | |