Braskem PE SEB853/72
| Категория | LDPE, Low Density Polyethylene |
| Производитель | Braskem America Inc. |
| Торговая марка | Braskem PE |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
qTr9GT_Braskem-PE-SEB853-72.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Description: SEB853/72 is a grade produced under high pressure technology. Films obtained with this product show outstanding optical properties, good sealability, and low gel amount. The minimum biobased content of this grade is 95%, determined according to ASTM D6866.
Additives: Slip Agent Medium. Antiblocking Agent Medium.
Applications: Lamination film; general purpose; automatic packaging of solids products (FFS).
Process: Blown Film Extrusion.
Additives: Slip Agent Medium. Antiblocking Agent Medium.
Applications: Lamination film; general purpose; automatic packaging of solids products (FFS).
Process: Blown Film Extrusion.
| Главная Информация | |
|---|---|
| Добавка |
|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.923 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 2.7 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 38 | µm | |
| Прочность на растяжение | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 30.0 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 20.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 270 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 1000 | % | ASTM D882 |
| Ударное падение Dart 1(38 µm, Blown Film) | 70 | g | ASTM D1709 |
| Elmendorf Tear Strength - TD (38 µm, Blown Film) | 100 | g | ASTM D1922 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (60 °, blown film) | 112 | ASTM D2457 | |
| Haze (Blown Film) | 5.0 | % | ASTM D1003 |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Двуслойное содержание | > 95 | % | ASTM D6866 |
| Blown Film Properties: 38µm thickness film, processed in a 75 mm screw diameter extruder with blow up ratio of 2:1, die gap 1.0 mmRecommended process conditions:Blown Film ExtrusionExtruder:Screw- relation L/D..........16 to 30:1Compression Ratio.........3 to 4:1Screw Package (Mesh)...40/60/40Temperature Profile: 1st zone............................110°C Extruder..........................150°C Die..................................160°C Blow up ratio...................from 2 to 3:1Frostline Height...............maximum equivalent to bubble diameter |
| Примечание | |
|---|---|
| 1 . | F50 |
| Тип материала | Категория | Производитель |
|---|---|---|
| Westlake LDPE EF677 | LDPE | Westlake Chemical Corporation |
| CRYSTALADD® HM-237 | LDPE | Ravago Manufacturing Americas, LLC |
| Lotrène® LDPE FE3000 | LDPE | QAPCO |
| Petrothene® NA340013 | LDPE | LyondellBasell Industries |
| MarFlex® 4553 | LDPE | Chevron Phillips Chemical Company LLC |
| MarFlex® 1013 | LDPE | Chevron Phillips Chemical Company LLC |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved