Описание материалов:
Poly (1, 4-butanediol Succinate) (hereunder PBS) is a kind of fully biodegradable macromolecular polymer that is synthesized from succinic acid and butanediol through a direct process of condensation polymerization. On specific conditions, this material can be finally decomposed safely and innoxiously into simple compounds such as CO2, H2O, etc.
PBS has predominant characteristics such as good thermal stability, fine mechanical and processing performance. It can be molding processed in normal plastic fabrication apparatus. Because of its excellent integrated performance, it also can be blended with other fully biodegradable plastic materials to modify the property to satisfy all kinds of manufacturing requirements of plastic products.
| Главная Информация | |
|---|
| Характеристики | - Обрабатываемость, хорошая
- Термическая стабильность, хорошая
- Биоразлагаемый
|
| Используется | - Упаковка
- Смешивание
- Сельскохозяйственное применение
- Медицинские принадлежности/принадлежности для ухода
|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | |
|---|
| Плотность | 1.15 - 1.25 | g/cm³ | |
| Массовый расход расплава (MFR) | < 8.0 | g/10 min | |
| Содержание золы | | % | |
| Тепловой | Номинальное значение | Единица измерения | |
|---|
| Heat Deflection Temperature | > 80 | °C | |
| Дополнительная информация | Номинальное значение | Единица измерения | |
|---|
| Потеря сушки | | % | |
| Механические | Номинальное значение | Единица измерения | |
|---|
| Прочность на растяжение (Break) | > 30.0 | MPa | |
| Удлинение при растяжении (Break) | > 300 | % | |
| Флекторный модуль | > 400 | MPa | |
| Flexural Strength | > 20.0 | MPa | |
| Воздействие | Номинальное значение | Единица измерения | |
|---|
| Зубчатый изод Impact | > 6.0 | kJ/m² | |
| Тепловой | Номинальное значение | Единица измерения | |
|---|
| Викат Температура размягчения | > 101 | °C | |
| Температура плавления | 43.3 - 48.9 | °C | |