Braskem PE LD7001A
| Категория | LDPE, Low Density Polyethylene |
| Производитель | Braskem |
| Торговая марка | Braskem PE |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
pYDOXz_Braskem-PE-LD7001A.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
LD7001A is a Low Density Polyethylene produced by High Pressure Process, in Autoclave reactor. Developed for the manufacturing of extruded films. It has high mechanical and impact strength, good processability, high ESCR and good shrinkage.
Additivation:
Application:
Coextruded and shrink films.
Process:
Recommended processing conditions for film extrusion about 200 - 220 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee.
Additivation:
- Antiblocking
- Slip agent
Application:
Coextruded and shrink films.
Process:
Recommended processing conditions for film extrusion about 200 - 220 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee.
| Главная Информация | |
|---|---|
| Добавка |
|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.921 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.34 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Прочность на растяжение | ASTM D882 | ||
| MD : Fracture, 38 µm | 30.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 25.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Fracture, 38 µm | 280 | % | ASTM D882 |
| TD : Fracture, 38 µm | 880 | % | ASTM D882 |
| Ударное падение Dart 1(38 µm) | 130 | g | ASTM D1709 |
| Elmendorf Tear Strength - TD (38 µm) | 130 | g | ASTM D1922 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (60°, 38.0 µm) | 61 | ASTM D2457 | |
| Haze | 19 | % | ASTM D1003 |
| Инструкции по впрыску |
|---|
| Recommended Coextrusion Conditions: Temperature Profile: 200°C to 220°C |
| Примечание | |
|---|---|
| 1 . | F50 |
| Тип материала | Категория | Производитель |
|---|---|---|
| TOTAL Polyethylene LDPE 1200 MN 18 C | LDPE | TOTAL Refining & Chemicals |
| Trithene® TS 9022 | LDPE | Petroquimica Triunfo |
| Borealis PE CA9150 | LDPE | Borealis AG |
| Braskem PE F-2022/0 | LDPE | Braskem |
| Kazan LDPE 153-12K | LDPE | Kazanorgsintez Joint Stock Company |
| TOTAL Polyethylene LDPE CD0230 | LDPE | TOTAL Refining & Chemicals |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved