Описание материалов:
Vydyne 88X-D is medium-viscosity PA66/6 random copolymer used for injection-molding applications. It provides benefits of high flow, fast cycles and good surface finish of the final parts. This copolymer is specifically designed to be used in application that requires high strength, good toughness, good surface lubricity and abrasion resistance.
Vydyne 88X-D is available in natural color, and it is the product of choice for low-yellowness-required applications. Vydyne 88X-D maintains the chemical resistance typical of PA66/6 to many chemicals, machine and motor oils, solvents and gasoline.
Typical Applications/End Uses:
Vydyne 88X-D has been used in many injection-molding applications such as cable ties/tie straps, terminal blocks, bearings, bushings, cams, electrical connectors and housings and many other hardware and general consumer-industrial parts.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Цикл быстрого формования
- Общее назначение
- Хороший выпуск пресс-формы
- Хорошая жесткость
- Высокая жесткость
- Смазка
- Ядро
|
| Используется | - Подшипники
- Камеры
- Разъемы
- Крепежные детали
- Общее назначение
- Корпуса
- Промышленное применение
|
| Рейтинг агентства | - Астм д 4066 PA0131
- Астм д 6779 PA0131
- FED L-P-410A
|
| Соответствие RoHS | |
| Номер файла UL | |
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Физический | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Плотность | 1.14 | -- | g/cm³ | ISO 1183 |
| Формовочная усадка | | | | ISO 294-4 |
| Across Flow
: 23°C, 2.00 mm | 1.8 | -- | % | |
| Flow
: 23°C, 2.00 mm | 1.8 | -- | % | |
| Поглощение воды | | | | ISO 62 |
| 23°C, 24 hr | 1.4 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.8 | -- | % | |
| Механические | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Модуль растяжения (23°C) | 3400 | 1800 | MPa | ISO 527-2 |
| Tensile Stress | | | | ISO 527-2 |
| Yield, 23°C | 86.0 | 60.0 | MPa | |
| Break, 23°C | 50.0 | 40.0 | MPa | |
| Растяжимое напряжение (Yield, 23°C) | 5.0 | 10 | % | ISO 527-2 |
| Номинальное растяжение при разрыве (23°C) | 27 | > 50 | % | ISO 527-2 |
| Флекторный модуль (23°C) | 2900 | 980 | MPa | ISO 178 |
| Flexural Strength (23°C) | 90.0 | 30.0 | MPa | ISO 178 |
| Poisson's Ratio | 0.40 | -- | | ISO 527-2 |
| Воздействие | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Ударная прочность | | | | ISO 179/1eA |
| -30°C | 5.0 | 5.0 | kJ/m² | |
| 23°C | 6.0 | 30 | kJ/m² | |
| Charpy Unnotched Impact Strength | | | | ISO 179/1eU |
| -30°C | No Break | No Break | | |
| 23°C | No Break | No Break | | |
| Зубчатый изод ударная прочность | | | | ISO 180 |
| -30°C | 5.0 | 5.0 | kJ/m² | |
| 23°C | 6.0 | 30 | kJ/m² | |
| Тепловой | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature | | | | |
| 0.45 MPa, Unannealed | 183 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 62.0 | -- | °C | ISO 75-2/A |
| Температура плавления | 253 | -- | °C | ISO 11357-3 |
| CLTE | | | | ISO 11359-2 |
| Flow
: 23 to 55°C, 2.00 mm | 1.0E-4 | -- | cm/cm/°C | |
| Transverse
: 23 to 55°C, 2.00 mm | 1.0E-4 | -- | cm/cm/°C | |
| RTI Elec | | | | UL 746 |
| 0.400 mm | 130 | -- | °C | |
| 0.710 mm | 130 | -- | °C | |
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C | |
| RTI Imp | | | | UL 746 |
| 0.400 mm | 75.0 | -- | °C | |
| 0.710 mm | 75.0 | -- | °C | |
| 1.50 mm | 75.0 | -- | °C | |
| 3.00 mm | 75.0 | -- | °C | |
| RTI Str | | | | UL 746 |
| 0.400 mm | 75.0 | -- | °C | |
| 0.710 mm | 85.0 | -- | °C | |
| 1.50 mm | 85.0 | -- | °C | |
| 3.00 mm | 85.0 | -- | °C | |
| Электрический | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Сопротивление громкости (0.750 mm) | 1.0E+10 | -- | ohms·cm | IEC 60093 |
| Диэлектрическая прочность (1.00 mm) | 26 | -- | kV/mm | IEC 60243 |
| Дуговое сопротивление (3.00 mm) | PLC 5 | -- | | ASTM D495 |
| Comparative Tracking Index (3.00 mm) | 600 | -- | V | IEC 60112 |
| Высокоусиленное дуговое зажигание (HAI) | | | | UL 746 |
| 0.710 mm | PLC 0 | -- | | |
| 1.50 mm | PLC 0 | -- | | |
| 3.00 mm | PLC 0 | -- | | |
| Высоковольтная скорость отслеживания дуги (HVTR) | PLC 0 | -- | | UL 746 |
| Зажигание горячей проволоки (HWI) | | | | UL 746 |
| 0.710 mm | PLC 4 | -- | | |
| 1.50 mm | PLC 3 | -- | | |
| 3.00 mm | PLC 3 | -- | | |
| Воспламеняемость | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Огнестойкость | | | | UL 94 |
| 0.400 mm | V-2 | -- | | |
| 0.710 mm | V-2 | -- | | |
| 1.50 mm | V-2 | -- | | |
| 3.00 mm | V-2 | -- | | |
| Индекс воспламеняемости провода свечения | | | | IEC 60695-2-12 |
| 0.710 mm | 800 | -- | °C | |
| 1.50 mm | 800 | -- | °C | |
| 3.00 mm | 930 | -- | °C | |
| Температура зажигания провода свечения | | | | IEC 60695-2-13 |
| 0.710 mm | 700 | -- | °C | |
| 1.50 mm | 700 | -- | °C | |
| 3.00 mm | 700 | -- | °C | |
| Индекс кислорода | 28 | -- | % | ISO 4589-2 |
| Инъекция | Сухой | Единица измерения | |
|---|
| Температура сушки | < 70.0 | °C | |
| Время сушки | 1.0 to 3.0 | hr | |
| Рекомендуемый Макс измельчения | 25 | % | |
| Задняя температура | 250 to 270 | °C | |
| Средняя температура | 260 to 275 | °C | |
| Передняя температура | 270 to 280 | °C | |
| Температура сопла | 270 to 290 | °C | |
| Температура обработки (расплава) | 275 to 290 | °C | |
| Температура формы | 65.0 to 95.0 | °C | |