Описание материалов:

Ixef® HC-1022 is a 50% glass-fiber reinforced, general purpose polyarylamide compound that exhibits very high strength and rigidity, outstanding surface gloss, and excellent creep resistance.

Ixef® HC-1022 shows no evidence of cytotoxicity, sensitization, intracutaneous reactivity or systemic toxicity based on biocompatibility testing as defined by ISO 10993:1. Solvay offers these materials for healthcare applications that require limited exposure (less than 24 hours) to the body

Black: HC-1022 BK 000

Natural: HC-1022 NT 000

Gray: HC-1022 GY51

Additional colors available

Custom colorable

Главная Информация
Наполнитель/армирование	Армированный стекловолокном материал, 50% наполнитель по весу
Характеристики	Супер жесткий Хорошая стабильность размеров Отличный внешний вид Низкая гигроскопичность Дезинфекция электронного пучка Радиоактивный Проницаемый Радиационная дезинфекция Высокая прочность Хорошая дезинфекция Дезинфекция оксида этилена Антигамма-излучение Хорошее сопротивление ползучести Высокая яркость Хорошая химическая стойкость Биологическая Совместимость Универсальный
Используется	Применение подсветки Хирургические инструменты Стоматологическое применение Медицинские принадлежности/принадлежности для ухода Медицинское оборудование Медицинские устройства
Рейтинг агентства	ISO 10993
Соответствие RoHS	Соответствие RoHS
Внешний вид	Черный Серый Доступные цвета Натуральный цвет
Формы	Частицы
Метод обработки	Литье под давлением

Физический	Сухой	Состояние	Единица измерения	Метод испытания
Плотность	1.64	--	g/cm³	ISO 1183
Формовочная усадка	0.10 - 0.30	--	%	ISO 294-4
Поглощение воды (23°C, 24 hr)	0.16	--	%	ISO 62
Поглощение воды- Equil, 65% RH	1.50	--		Internal method

Механические	Сухой	Состояние	Единица измерения	Метод испытания
Модуль растяжения	19500	19500	MPa	ISO 527-2
Tensile Stress (Break)	280	260	MPa	ISO 527-2
Растяжимое напряжение (Break)	1.9	2.2	%	ISO 527-2
Флекторный модуль	18500	--	MPa	ISO 178
Флекторный стресс	380	--	MPa	ISO 178

Воздействие	Сухой	Состояние	Единица измерения	Метод испытания
Зубчатый изод Impact	110	--	J/m	ASTM D256
Незубчатый изод Impact	850	--	J/m	ASTM D256

Тепловой	Сухой	Состояние	Единица измерения	Метод испытания
Heat Deflection Temperature (1.8 MPa, Unannealed)	230	--	°C	ISO 75-2/A
CLTE- Поток	1.5E-5	--	cm/cm/°C	ISO 11359-2

Инъекция	Сухой	Единица измерения
Температура сушки	120	°C
Время сушки	0.50 - 1.5	hr
Задняя температура	250 - 260	°C
Передняя температура	260 - 290	°C
Температура сопла	260 - 290	°C
Температура обработки (расплава)	280	°C
Температура формы	120 - 140	°C
Скорость впрыска	Fast

Инструкции по впрыску
Hot runners: 250°C to 260°C (482°C to 500°F)StorageIxef® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Ixef® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Ixef® processing guide.DryingThe material as supplied is ready for molding without drying. However, If the bags have been open for longer than 24 hours, the material needs to be dried. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C (212°F), or 1-7 hours at 80°C (176°F).Injection MoldingIxef® HC-1022 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure.The measured melt temperature should be about 280°C (536°F), and the barrel temperatures should be around 250 to 260°C (482 to 500°F) in the rear zone, gradually increasing to 260 to 290°C (500 to 554°F) in the front zone. If hot runners are used, they should be set to 250 to 260°C (482 to 500°F).To maximize crystallinity, the temperature of the mold cavity surface must be held between 120 and 140°C (248 and 284°F). Molding at lower temperatures will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled (95-99%).

Инструкции по впрыску

Hot runners: 250°C to 260°C (482°C to 500°F)StorageIxef® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Ixef® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Ixef® processing guide.DryingThe material as supplied is ready for molding without drying. However, If the bags have been open for longer than 24 hours, the material needs to be dried. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C (212°F), or 1-7 hours at 80°C (176°F).Injection MoldingIxef® HC-1022 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure.The measured melt temperature should be about 280°C (536°F), and the barrel temperatures should be around 250 to 260°C (482 to 500°F) in the rear zone, gradually increasing to 260 to 290°C (500 to 554°F) in the front zone. If hot runners are used, they should be set to 250 to 260°C (482 to 500°F).To maximize crystallinity, the temperature of the mold cavity surface must be held between 120 and 140°C (248 and 284°F). Molding at lower temperatures will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled (95-99%).

Тип материала	Категория	Производитель
Ixef® DW-1022	PARA	Solvay Specialty Polymers
Nylon-MXD6 K7007C	PARA	Mitsubishi Gas Chemical America, Inc.
Reny® 1021UCS	PARA	Mitsubishi Engineering-Plastics Corp
Reny® 1032H	PARA	Mitsubishi Engineering-Plastics Corp
Reny® 1022HS	PARA	Mitsubishi Engineering-Plastics Corp
Ixef® 2030	PARA	Solvay Specialty Polymers