Ixef® DW-1022

Категория	PARA, Polyarylamide
Производитель	Solvay Specialty Polymers
Торговая марка	Ixef®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	MbAB7G_Ixef-DW-1022.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

Ixef® DW-1022 is a 50% glass-fiber reinforced, general purpose polyarylamide compound that exhibits very high strength and rigidity, outstanding surface gloss, and excellent creep resistance.

Ixef® DW-1022 is approved for use in potable water in France, Germany, the United States and the United Kingdom.

Black: DW-1022 BK 000

Natural: DW-1022 NT 000

Главная Информация
Наполнитель/армирование	Армированный стекловолокном материал, 50% наполнитель по весу
Характеристики	Супер жесткий Хорошая стабильность размеров Отличный внешний вид Низкая гигроскопичность Высокая прочность Хорошая дезинфекция Хорошее сопротивление ползучести Высокая яркость Хорошая химическая стойкость Универсальный
Используется	Электроприборы Применение подсветки Медицинское оборудование Применение питьевой воды
Рейтинг агентства	ACS не рассчитан DVGW W270 FDA 21 CFR 176,170, таблица 2, статус C FDA 21 CFR 176,170, таблица 2, Статус B FDA 21 CFR 176,170, таблица 2, статус D FDA 21 CFR 176,170, таблица 2, статус G FDA 21 CFR 176,170, таблица 2, статус F FDA 21 CFR 176,170, таблица 2, статус H KTW не Номинальная 3 Утверждено NSF 61 4 WRAS не Номинальный при 85 °C Европа без 10/2011
Соответствие RoHS	Соответствие RoHS
Внешний вид	Черный Натуральный цвет
Формы	Частицы
Метод обработки	Литье под давлением

Физический	Сухой	Состояние	Единица измерения	Метод испытания
Плотность	1.64	--	g/cm³	ISO 1183
Формовочная усадка	0.10 - 0.30	--	%	ISO 294-4
Поглощение воды (23°C, 24 hr)	0.16	--	%	ISO 62

Механические	Сухой	Состояние	Единица измерения	Метод испытания
Модуль растяжения	19500	19500	MPa	ISO 527-2
Tensile Stress (Break)	280	260	MPa	ISO 527-2
Растяжимое напряжение (Break)	1.9	2.2	%	ISO 527-2
Флекторный модуль	18500	--	MPa	ISO 178
Флекторный стресс	380	--	MPa	ISO 178

Воздействие	Сухой	Состояние	Единица измерения	Метод испытания
Зубчатый изод Impact	110	--	J/m	ASTM D256
Незубчатый изод Impact	850	--	J/m	ASTM D256

Тепловой	Сухой	Состояние	Единица измерения	Метод испытания
Heat Deflection Temperature (1.8 MPa, Unannealed)	230	--	°C	ISO 75-2/A
CLTE- Поток	1.5E-5	--	cm/cm/°C	ISO 11359-2

Дополнительная информация	Сухой	Состояние
Поглощение воды- Equil, 65% RH	--

Инъекция	Сухой	Единица измерения
Температура сушки	120	°C
Время сушки	0.50 - 1.5	hr
Задняя температура	250 - 260	°C
Передняя температура	260 - 290	°C
Температура сопла	260 - 290	°C
Температура обработки (расплава)	280	°C
Температура формы	120 - 140	°C
Скорость впрыска	Fast

Инструкции по впрыску
Hot runners: 250°C to 260°C (482°C to 500°F)StorageIxef® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Ixef® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Ixef® processing guide.DryingThe material as supplied is ready for molding without drying. However, If the bags have been open for longer than 24 hours, the material needs to be dried. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C (212°F), or 1-7 hours at 80°C (176°F).Injection MoldingIxef® DW-1022 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure.The measured melt temperature should be about 280°C (536°F), and the barrel temperatures should be around 250 to 260°C (482 to 500°F) in the rear zone, gradually increasing to 260 to 290°C (500 to 554°F) in the front zone. If hot runners are used, they should be set to 250 to 260°C (482 to 500°F).To maximize crystallinity, the temperature of the mold cavity surface must be held between 120 and 140°C (248 and 284°F). Molding at lower temperatures will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled (95-99%).

Инструкции по впрыску

Hot runners: 250°C to 260°C (482°C to 500°F)StorageIxef® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Ixef® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Ixef® processing guide.DryingThe material as supplied is ready for molding without drying. However, If the bags have been open for longer than 24 hours, the material needs to be dried. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C (212°F), or 1-7 hours at 80°C (176°F).Injection MoldingIxef® DW-1022 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure.The measured melt temperature should be about 280°C (536°F), and the barrel temperatures should be around 250 to 260°C (482 to 500°F) in the rear zone, gradually increasing to 260 to 290°C (500 to 554°F) in the front zone. If hot runners are used, they should be set to 250 to 260°C (482 to 500°F).To maximize crystallinity, the temperature of the mold cavity surface must be held between 120 and 140°C (248 and 284°F). Molding at lower temperatures will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled (95-99%).

Тип материала	Категория	Производитель
RTP 208 K	PARA	RTP Company
Reny® 1722F	PARA	Mitsubishi Engineering-Plastics Corp
Reny® G16S	PARA	Mitsubishi Engineering-Plastics Corp
Reny® 4501	PARA	Mitsubishi Engineering-Plastics Corp
Reny® 2505	PARA	Mitsubishi Engineering-Plastics Corp
Ixef® 2030	PARA	Solvay Specialty Polymers

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

