Описание материалов:
MDF-137 is a certified prime grade Hexene copolymer MEDIUM MOLECULAR WEIGHT developed for production of thin gauged paper-like Blown films. MDF-137 features BROAD molecular weight distribution for improved processability in HMW high stalk equipment or in conventional film lines equipped with die gap = 0.75 to 1.25 = mm., excellent melt strength, easy film drawdown, and optimal overall balance of thin film mechanical properties: stiffness, tensile, Elmendorf tear, and Dart impact strength. MDF-137 applications include merchandise, produce, and trash bags, shopping bags, small shoppers, lamination films, wrapping films, and tablecloths. Minimum recommended film thickness is 12 microns (0.5 mil), and melt processing temperature 195° to 220° C. MDF-137 complies with FDA regulation 21CFR 177.1520 (c) 3.2(a) and most international regulations concerning the use of Polyethylene in contact with food articles.
| Главная Информация | |
|---|
| Характеристики | - Жесткий, хороший
- Гексен-комномер
- Обрабатываемость, хорошая
- Широкое молекулярное распределение веса
- Хорошее Отшелушивание
- Хорошая прочность
- Хорошая прочность расплава
- Хорошая прочность на разрыв
- Соответствие пищевого контакта
- Средний Молекулярный вес
|
| Используется | |
| Рейтинг агентства | - FDA 21 CFR 177,1520 (c) 3.2a
|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.937 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) | | | ASTM D1238 |
| 190°C/2.16 kg | 0.30 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 20 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 13 | µm | |
| Толщина пленки-рекомендовано/доступно | Minimum 12 µm (0.5 mil) | | |
| Сектантный модуль 1 | | | ASTM D882 |
| 1% secant, MD
: 13 µm | 790 | MPa | ASTM D882 |
| 1% secant, TD
: 13 µm | 965 | MPa | ASTM D882 |
| Прочность на растяжение 2 | | | ASTM D882 |
| MD
: Yield, 13 µm | 21.0 | MPa | ASTM D882 |
| TD
: Yield, 13 µm | 21.0 | MPa | ASTM D882 |
| MD
: Broken, 13 µm | 42.0 | MPa | ASTM D882 |
| TD
: Broken, 13 µm | 41.0 | MPa | ASTM D882 |
| Удлинение при растяжении 3 | | | ASTM D882 |
| MD
: Broken, 13 µm | 500 | % | ASTM D882 |
| TD
: Broken, 13 µm | 600 | % | ASTM D882 |
| Ударное падение Dart 4(13 µm) | 110 | g | ASTM D1709A |
| Elmendorf Tear Strength | | | ASTM D1922 |
| MD
: 13 µm | 50 | g | ASTM D1922 |
| TD
: 13 µm | 500 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Пиковая температура плавления | 125 | °C | ASTM D3417 |
| Дополнительная информация |
|---|
| Film Specimen: 0.5 mil (13 µm) film, melt temperature 410-430°F (210-220°C), blow-up-ratio 4.0:1, frost line height 8 x die ø. |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 195 - 220 | °C | |
| Примечание |
|---|
| 1 . | Compression molded |
| 2 . | Compression molded |
| 3 . | Compression molded |
| 4 . | F50 |