AXELERON™ FO 8864 BK CPD

Категория MDPE, Black Medium Density Polyethylene Compound for Cable Jacketing
Производитель The Dow Chemical Company
Торговая марка AXELERON™
Порт Китай Шанхайский порт
Торговые условия FOB, CFR, CIF
Платежное средство L/C, T/T, Western Union
PDF IrvENG_AXELERON-FO-8864-BK-CPD.pdf
Контактная информация
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Описание материалов:
Dow AXELERON™FO 8864 BK CPD is a high molecular weight, linear, medium density, black polyethylene material, which is developed for the application of optical fiber and ordinary metal conductor cable sheath. This material has very good processing characteristics and can be made into a very strong cable sheath. Dow's AXELERON™FO 8864 BK CPD also has excellent environmental stress cracking resistance, weather resistance and thermal oxidation degradation resistance.

Dow AXELERON™FO 8864 BK CPD provides excellent low temperature optical signal attenuation performance in the application field of optical fiber cable sheath. The material combines reduced extrusion retraction stress with excellent tensile modulus. Therefore, the contraction force exerted by the cable sheath on the fiber optic cable during the temperature cycle change is minimized.

Specifications
Dow AXELERON™FO 8864 BK CPD meets the requirements of the following raw material specifications:
  • ASTM D 1248: Type II, Class C, Class 4, E9 and J4
  • Federal LP-390C: Type III, M, 2, 3, 4
  • REA PE 39 and 89 (raw material section)
Главная Информация
Используется
  • Волоконно-оптический кабель с гнездом
  • Кабельная оболочка
  • Применение проводов и кабелей
  • Волоконно-оптический кабель
Рейтинг агентства
  • ASTM D 1248, II, Class C, Cat. 4
  • FED L-P-390C, Тип III, класс M, категория 4, класс 3
  • REA PE-39
  • REA PE-89
Формы
  • Частицы
ФизическийНоминальное значениеЕдиница измеренияМетод испытания
Удельный вес 0.941g/cm³ASTM D792
Массовый расход расплава (MFR) (190°C/2.16 kg)0.70g/10 minASTM D1238
Экологическое сопротивление растрескиванию (10% Igepal, F0)> 1000hrASTM D1693
Содержание черного углерода 2.6%ASTM D1603
Коэффициент поглощения- (KAB/m) > 400ASTM D3349
МеханическиеНоминальное значениеЕдиница измеренияМетод испытания
Модуль растяжения- 1% Secant 1ASTM D638
    -40°C 1030MPaASTM D638
    -20°C 793MPaASTM D638
    0°C 552MPaASTM D638
    20°C 310MPaASTM D638
    40°C 206MPaASTM D638
    60°C 124MPaASTM D638
Прочность на растяжение 228.3MPaASTM D638
Удлинение при растяжении 3(Break)800%ASTM D638
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Температура ломкости ASTM D746
    -- 4< -100°CASTM D746
    -- 5-65.0°CASTM D746
CLTE- Поток 6ASTM D696
    -40°C 1.0E-4cm/cm/°CASTM D696
    -20°C 1.4E-4cm/cm/°CASTM D696
    0°C 1.4E-4cm/cm/°CASTM D696
    20°C 2.0E-4cm/cm/°CASTM D696
    40°C 2.4E-4cm/cm/°CASTM D696
    60°C 2.8E-4cm/cm/°CASTM D696
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Диэлектрическая прочность 20kV/mmASTM D149
Диэлектрическая постоянная 2.50ASTM D1531
Коэффициент рассеивания 3.0E-4ASTM D1531
ЭкструзияНоминальное значениеЕдиница измерения
Температура расплава 232°C
Инструкции по экструзии
AXELERON™ FO 8864 BK CPD has good extrusion processing latitude. High, stable output rates and moderate melt temperatures and pressures are obtainable with both polyethylene barrier and metering type extruder screws. Typical extrusion conditions are listed below; the exact conditions will depend upon the equipment used and the application.Extruder Screw Type: PE Metering Screw LD: 18:1 to 24:1 Compression Ratio: 2.5:1 to 3.0:1 Screen Pack: 20/40/60/20 mesh Temperature Profile Hopper: Water Cooling Feed Zone: 300°F (150°C) Center Zones: 440°F (225°C) Metering Zone: 440°F (225°C) Head: 440°F (225°C) Die: 440°F (225°C) Melt Temperature: 450°F (230°C) AXELERON™ FO 8864 BK CPD cable jacketing can be applied with either pressure or sleeving (tube-on) type extrusion tooling. With tube-on extrusion, a minimum tubing tip diameter and a 2:1 drawdown ratio is recommended. If necessary, a higher drawdown ratio can be used to increase jacket tightness.
Примечание
1 .Reduced testing speed of 0.10 inch/min (2.5 mm/min) with an initial 1.50 inch (38mm) jaw separation. Modulus data will vary with testing speed. Unless otherwise noted, amples are tested in accordance with ASTM D 1248, "Polyethylene Plastics Molding and Extrusion Materials."
2 .Type 4, 50mm/min
3 .Type 4, 50mm/min
4 .Notched, F20
5 .Notched, F50
6 .COE data generated on Dupont 942 Thermomechanical Analyzer.
Тип материала Категория Производитель
TOTAL Polyethylene Lumicene® Supertough 32ST05 MDPE TOTAL Refining & Chemicals
BorPEX™ ME2592 MDPE Borealis AG
BorSafe™ ME3440-D MDPE Borealis AG
HANWHA CMBA-8240BK MDPE Hanwha Chemical
Lupolen 4021 K RM MDPE LyondellBasell Industries
Epolene® E-20 MDPE Westlake Chemical Corporation
Получите информацию об этом продукте следующим способом.
Телефон+086 13424755533
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Copyright © russianpolymer.com All Rights Reserved
Получите информацию об этом продукте следующим способом.
+08613424755533
sales@su-jiao.com

Служба поддержки клиентов Вичат
Свяжитесь с нами