DOW™ LDPE 410E
| Категория | LDPE, Low Density Polyethylene Resin |
| Производитель | The Dow Chemical Company |
| Торговая марка | DOW™ LDPE |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
lXQA0r_DOW-LDPE-410E.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
DOW LDPE 410E low density polyethylene resin is a high transparency resin, used for composite film and high transparency packaging film processing. The resin does not contain slip agent and opening agent, and can be extruded by a common blown film process. The processing melting temperature is between 170 and 195°C, and the melt temperature of the cast film is between 180 and 240°C. At the time of preparation, this resin has the characteristics of excellent processability and drafting properties, excellent toughness and impact resistance, excellent optical properties, and excellent tensile strength and tear strength.
Application field:
Complies with:
Application field:
- composite film
- food packaging film
- Sanitary film
- cast film
- Bubble film
- Foamed PE
- Extrusion coating
Complies with:
- U.S. FDA 21 CFR 177.1520(c)2.2
- EU, No 10/2011
| Главная Информация | |
|---|---|
| Рейтинг агентства |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.925 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Коэффициент трения (vs. Itself - Dynamic) | 0.60 - 0.80 | ASTM D1894 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 50 | µm | |
| Сектантный модуль | ASTM D882 | ||
| 2% secant, MD : 50 µm | 190 | MPa | ASTM D882 |
| 2% secant, TD : 50 µm | 200 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 50 µm | 10.0 | MPa | ASTM D882 |
| TD : Yield, 50 µm | 11.0 | MPa | ASTM D882 |
| MD : Break, 50 µm | 22.0 | MPa | ASTM D882 |
| TD : Break, 50 µm | 20.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Break, 50 µm | 450 | % | ASTM D882 |
| TD : Break, 50 µm | 650 | % | ASTM D882 |
| Ударное падение Dart (50 µm) | 110 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm | 500 | g | ASTM D1922 |
| TD : 50 µm | 400 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Викат Температура размягчения | 96.0 | °C | ISO 306/A |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (20°, 50.0 µm) | 80 | ASTM D2457 | |
| Haze (50.0 µm) | 6.9 | % | ASTM D1003 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура расплава | 170 - 195 | °C |
| Инструкции по экструзии |
|---|
| 放大比 1:2.5 |
| Тип материала | Категория | Производитель |
|---|---|---|
| SABIC® LDPE 2102N0W | LDPE | Saudi Basic Industries Corporation (SABIC) |
| MIDILENA I XCF-2 | LDPE | ROMPETROL PETROCHEMICALS S.R.L. |
| AEI SX490:CM401 and SX490:CM401-2 | LDPE | AEI Compounds Limited |
| Daelim Po1y® LD-01A | LDPE | DAELIM INDUSTRIAL CO., LTD. |
| Petrothene® NA204000 (Extrusion Coating) | LDPE | LyondellBasell Industries |
| Petrothene® NA942094 | LDPE | LyondellBasell Industries |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved