Описание материалов:
Viton® AL-300 is an "AL-family" gum polymer that demonstrates improved processing when compared to its precursor Viton B-70N. This gum provides:
-Lower viscosity
-Improved mold flow
-Better mold release
-Less mold fouling
-Improved compression set resistance, and
-Good low temperature characteristics
Applications:
-Fuel systems, such as fuel injectors O-rings
-Injection and transfer molding of O-rings, gaskets, and other sealing devices
-Extruded cords, profiles and tubing, or calendered sheets, when a blend of gum polymers are used
-Solution coatings of fabrics and other substrates
-Lower viscosity
-Improved mold flow
-Better mold release
-Less mold fouling
-Improved compression set resistance, and
-Good low temperature characteristics
Applications:
-Fuel systems, such as fuel injectors O-rings
-Injection and transfer molding of O-rings, gaskets, and other sealing devices
-Extruded cords, profiles and tubing, or calendered sheets, when a blend of gum polymers are used
-Solution coatings of fabrics and other substrates
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Внешний вид |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 1.77 | g/cm³ | ASTM D792 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Твердость дюрометра (Shore A) | 71 | ASTM D2240 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Tensile Stress (100% Strain) | 5.10 | MPa | ASTM D412 |
| Прочность на растяжение (Break) | 11.6 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 220 | % | ASTM D412 |
| Tear Strength 1(23°C) | 21.5 | kN/m | ASTM D624 |
| Комплект сжатия (200°C, 70 hr) | 25 | % | ASTM D395 |
| Старение | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Изменение прочности на растяжение в воздухе | ASTM D573 | ||
| 200°C, 70 hr | -2.6 | % | ASTM D573 |
| 100% strain, 200°C, 70 hr | 9.8 | % | ASTM D573 |
| 200°C, 168 hr | 11 | % | ASTM D573 |
| 100% strain, 200°C, 168 hr | 18 | % | ASTM D573 |
| 250°C, 70 hr | 6.0 | % | ASTM D573 |
| 100% strain, 250°C, 70 hr | -29 | % | ASTM D573 |
| 250°C, 168 hr | -2.6 | % | ASTM D573 |
| 100% strain, 250°C, 168 hr | 3.9 | % | ASTM D573 |
| Изменение максимального удлинения в воздухе | ASTM D573 | ||
| 200°C, 70 hr | -7.0 | % | ASTM D573 |
| 200°C, 168 hr | -4.7 | % | ASTM D573 |
| 250°C, 70 hr | -2.3 | % | ASTM D573 |
| 250°C, 168 hr | 0.0 | % | ASTM D573 |
| Изменение твердости дюрометра в воздухе | ASTM D573 | ||
| Support a, 200°C, 70 hr | 2.0 | ASTM D573 | |
| Support a, 200°C, 168 hr | 1.0 | ASTM D573 | |
| Support a, 250°C, 70 hr | 0.0 | ASTM D573 | |
| Support a, 250°C, 168 hr | 71 | ASTM D573 | |
| Изменение прочности на растяжение | ASTM D471 | ||
| 23°C, 168 hr, in reference fuel I | -50 | % | ASTM D471 |
| 100% strain, 23°C, 168 hr, in reference fuel I | -27 | % | ASTM D471 |
| 200°C, 70 hr, in IRM 903 oil | 3.4 | % | ASTM D471 |
| 100% strain, 200°C, 70 hr, in IRM 903 oil | 0.0 | % | ASTM D471 |
| Изменение максимального удлинения | ASTM D471 | ||
| 23°C, 168 hr, in reference fuel I | -28 | % | ASTM D471 |
| 200°C, 70 hr, in IRM 903 oil | 7.0 | % | ASTM D471 |
| Изменение твердости дюрометра | ASTM D471 | ||
| Support A, 23°C, 168 hr, in reference fuel I | -20 | ASTM D471 | |
| Support A, 200°C, 70 hr, in IRM 903 oil | -1.0 | ASTM D471 | |
| Изменение объема | ASTM D471 | ||
| 23°C, 168 hr, in reference fuel I | 36 | % | ASTM D471 |
| 200°C, 70 hr, in IRM 903 oil | 3.5 | % | ASTM D471 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Температура перехода стекла | -19.5 | °C | DSC |
| Дополнительная информация |
|---|
| Mooney Scorch, MS +1 at 121°C, Minimum Viscosity: 30Mooney Scorch, MS at 121°C, units rise at 30 min: 0.0MDR at 177°C, Micro Die, 0.5° Arc, 6 min motor:Minimum Torque, ML: 0.8 in-lbScorch Time, ts2: 1.0 minMaximum Torque, MH: 17.9 in-lbOptimum Cure Time, tc90: 2.4 minMDR at 177°C, Micro Die, 3° Arc, 12 min motor:Minimum Torque, ML: 0.839 minMaximum Torque, MH: 82.0 in-lbOptimum Cure Time, tc90: 3.8 minTemperature Retraction Test, ASTM D1329-88, TR-10: -19°CNominal Viscosity, ML 1 + 10, 121°C: 30Polymer Fluorine Content: 66% |
| Примечание | |
|---|---|
| 1 . | C mould |
| Тип материала | Категория | Производитель |
|---|---|---|
| Viton® GF-600S | Fluorelastomer | DuPont Performance Elastomers |
| Boda BDF25CP | Fluorelastomer | Chenguang Fluoro & Silicone Elastomers Co., Ltd. |
| Fluran F-5500-A | Fluorelastomer | Saint Gobain - Norton |
| FPD Blue™ 707 | Fluorelastomer | Greene, Tweed & Co. |
| 3M™ Dyneon™ Fluoroelastomer FE 5642 | Fluorelastomer | 3M Advanced Materials Division |
| 3M™ Dyneon™ Fluoroelastomer FE 5530 | Fluorelastomer | 3M Advanced Materials Division |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved