DynaMix™ XP-66LGR

Категория PA66, Polyamide 66 Alloy , Nylon 66 Alloy
Производитель Polymer Dynamix
Торговая марка DynaMix™
Порт Китай Шанхайский порт
Торговые условия FOB, CFR, CIF
Платежное средство L/C, T/T, Western Union
PDF hgKkHZ_DynaMix-XP-66LGR.pdf
Контактная информация
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Описание материалов:
Glass Filled PA 66 Alloy

Features:
  • High Heat Resistance
  • Great Dimensional Stability
  • Low Warpage
  • High Flow

Applications:
  • Aviation
  • Industrial
  • Metal and Long Glass Replacement
  • Automotive
  • Sporting Goods
Главная Информация
Наполнитель/армирование
  • Стекловолокно
Характеристики
  • Хорошая стабильность размеров
  • Высокий поток
  • Высокая термостойкость
  • Низкий уровень защиты
Используется
  • Применение самолетов
  • Автомобильные Приложения
  • Промышленное применение
  • Замена металла
ФизическийНоминальное значениеЕдиница измеренияМетод испытания
Удельный вес 1.75g/cm³ASTM D792
МеханическиеНоминальное значениеЕдиница измеренияМетод испытания
Модуль растяжения ASTM D638
    -- 118600MPa
    -- 23800MPa
Прочность на растяжение ASTM D638
    Break 2193MPa
    Break 293MPa
Удлинение при растяжении ASTM D638
    Break 33.4%
    Break 2.3%
Флекторный модуль ASTM D790
    -- 415500MPa
    -- 20700MPa
Flexural Strength 5310MPaASTM D790
ВоздействиеНоминальное значениеЕдиница измеренияМетод испытания
Зубчатый изод Impact ASTM D256
    -- 61500J/m
    -- 130J/m
Незубчатый изод Impact ASTM D256
    -- 7120J/m
    -- 1200J/m
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Температура отклонения при нагрузке (1.8 MPa, Unannealed)> 250°CASTM D648
Температура плавления 260°C
Примечание
1 .50% Rh specimen accelerated conditioning was conducted in accordance to modified ISO-1110 procedure Specimens were conditioned in sealed chamber at 70°C and 50% Rh for at least 2 weeks.
2 .50% Rh specimen accelerated conditioning was conducted in accordance to modified ISO-1110 procedure Specimens were conditioned in sealed chamber at 70°C and 50% Rh for at least 2 weeks.
3 .50% Rh specimen accelerated conditioning was conducted in accordance to modified ISO-1110 procedure Specimens were conditioned in sealed chamber at 70°C and 50% Rh for at least 2 weeks.
4 .50% Rh specimen accelerated conditioning was conducted in accordance to modified ISO-1110 procedure Specimens were conditioned in sealed chamber at 70°C and 50% Rh for at least 2 weeks.
5 .50% Rh specimen accelerated conditioning was conducted in accordance to modified ISO-1110 procedure Specimens were conditioned in sealed chamber at 70°C and 50% Rh for at least 2 weeks.
6 .50% Rh specimen accelerated conditioning was conducted in accordance to modified ISO-1110 procedure Specimens were conditioned in sealed chamber at 70°C and 50% Rh for at least 2 weeks.
7 .50% Rh specimen accelerated conditioning was conducted in accordance to modified ISO-1110 procedure Specimens were conditioned in sealed chamber at 70°C and 50% Rh for at least 2 weeks.
Тип материала Категория Производитель
TORZEN® HV240A NC01 Nylon 66 INVISTA Engineering Polymers
SHINSTRA WG30F Nylon 66 Shinil Chemical Industry Co., Ltd.
RTP 281 TFE 20 Nylon 66 RTP Company
Vydyne® M344 BLK Nylon 66 Ascend Performance Materials Operations LLC
LNP™ VERTON™ RV00AES compound Nylon 66 SABIC Innovative Plastics
LNP™ THERMOCOMP™ RF0029S compound Nylon 66 SABIC Innovative Plastics
Получите информацию об этом продукте следующим способом.
Телефон+086 13424755533
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Copyright © russianpolymer.com All Rights Reserved
Получите информацию об этом продукте следующим способом.
+08613424755533
sales@su-jiao.com

Служба поддержки клиентов Вичат
Свяжитесь с нами