BMC 2201 molding compound is a mineral filled, glass-fiber-and nylon-floc reinforced alkyd compound suitable for compression and transfer molding. It was developed for applications requiring better abrasion resistance than that available with other BMC products. BMC 2201 molding compound is produced in extruded form in a range of industrial colors. It is available in logs up to 12 inches in length or as precut slugs, of specific weight, in diameters from ¾ " to 2 7/8 ". Within this range smaller diameters are supplied as multiple extrusions and weight tolerances are plus or minus 5% up to a maximum of of plus 15 grams.
Главная Информация
Наполнитель/армирование
Стекло \ минеральное
Нейлоновое волокно
Характеристики
Хорошая стойкость к истиранию
Внешний вид
Доступные цвета
Формы
BMC-формовочная смесь
Метод обработки
Прессформа сжатия
Физический
Номинальное значение
Единица измерения
Метод испытания
Удельный вес
2.09
g/cm³
ASTM D792
Формовочная усадка-
Поток
0.30 to 0.60
%
ASTM D955
Поглощение воды (23°C, 24 hr)
0.30
%
ASTM D570
Твердость
Номинальное значение
Единица измерения
Метод испытания
Твердость барколя
65
ASTM D2583
Механические
Номинальное значение
Единица измерения
Метод испытания
Flexural Strength
121
MPa
ASTM D790
Прочность на сжатие
176
MPa
ASTM D695
Воздействие
Номинальное значение
Единица измерения
Метод испытания
Зубчатый изод Impact
160
J/m
ASTM D256
Тепловой
Номинальное значение
Единица измерения
Метод испытания
Температура отклонения при нагрузке (1.8 MPa, Unannealed)