AGILITY™ 1021 Performance LDPE
| Категория | LDPE, Low Density Polyethylene Resin |
| Производитель | The Dow Chemical Company |
| Торговая марка | AGILITY™ |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
gABY5d_AGILITY-1021-Performance-LDPE.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
AGILITY™ 1021 Performance LDPE is a high pressure LDPE resin designed to run at faster output rates on blown film lines in LLDPE rich blends while maintaining optics.
Main Characteristics:
Complies with:
Main Characteristics:
- Faster processing LDPE resin
- Designed for higher output rates in blends with LLDPE resins at 20-30% loading - Optimized molecular structure gives improved optics in blends with LLDPE resins
Complies with:
- EU No 10/2011
- U.S.FDA 21 CFR 177.1520 (c) 2.2
- Canadian HPFB No Objection
| Главная Информация | |
|---|---|
| Рейтинг агентства |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.919 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 1.9 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 51 | µm | |
| Сопротивление проколу пленки (51 µm) | 4.87 | J/cm³ | Internal method |
| Прочность пленки | ASTM D882 | ||
| MD : 51 µm | 45.8 | J/cm³ | ASTM D882 |
| TD : 51 µm | 60.1 | J/cm³ | ASTM D882 |
| Сектантный модуль | ASTM D882 | ||
| 2% secant, MD : 51 µm | 168 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 185 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 51 µm | 10.9 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 10.8 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 21.6 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 16.4 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Fracture, 51 µm | 260 | % | ASTM D882 |
| TD : Fracture, 51 µm | 540 | % | ASTM D882 |
| Ударное падение Dart (51 µm) | 100 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 460 | g | ASTM D1922 |
| TD : 51 µm | 250 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Температура плавления (DSC) | 108 | °C | Internal method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 50.8 µm) | 60 | ASTM D2457 | |
| Haze (50.8 µm) | 9.0 | % | ASTM D1003 |
| Инструкции по экструзии |
|---|
| Fabrication Conditions For Blown Film: Screw Size: 3.5 in.; 30:1 ratio L/D Screw Type: DSB II Die Gap: 70 mil (1.78 mm) Melt Temperature: 404°F (206°C) Output: 16 lb/hr/in. of die circumference Die Diameter: 8 in. Blow-Up Ratio: 2.5 to 1 Screw Speed: 50 rpm Frost Line Height: 42 in. (1067 mm) IBC |
| Тип материала | Категория | Производитель |
|---|---|---|
| Ravalene CR L 5241 | LDPE | Ravago Group |
| Sanren N110 (On-spec.) | LDPE | SINOPEC Shanghai Petrochemical Co. Ltd. |
| Sasol Polymers PE LT750 | LDPE | Sasol Polymers |
| Delta LDPE 2208 | LDPE | Delta Polymers |
| DOW™ Electrical & Telecommunications DFDA-1254 NT | LDPE | The Dow Chemical Company |
| ExxonMobil™ LDPE LD 419.MV | LDPE | ExxonMobil Chemical |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved